Enhanced Cathode/Electrolyte Interface by a Nano-Modified Barrier Layer for Solid Oxide Fuel Cells
Qiuqiu Lyu,Tenglong Zhu,Zongxun Li,Kaihua Sun,Chao Jin,Minfang Han,Hongxia Qu,Qin Zhong
DOI: https://doi.org/10.2139/ssrn.4102772
2022-01-01
Abstract:It’s a critical issue for the successful commercialization of solid oxide fuel cells (SOFCs) to achieve long-term thermal stability without significant performance degradation. Current work reports a cost-competitive and scalable method for modifying porous Gadolinia doped ceria (GDC) barrier layers, to obtain an almost-dense, sintering-active, and Sr-blocking cathode/electrolyte interface, by growing nanoparticles in-situ on porous surfaces. The cell performance only deteriorates by ~0.5% after 20 times thermal cycles as the temperature fluctuated between 200 and 750 ℃, which is more prominent enhancement than ~16% for pristine cell, and exhibits higher initial performance. The hydrothermal modified symmetric cell shows ~60% polarization resistance decrease and well-attached cathode/electrolyte interfaces after ~1200 hours of operation, exhibiting excellent stability while the pristine cell interfaces peeled off. The performance improvements and prolonged operation mechanisms are discussed and mainly attributed to the almost-dense barrier layer and robust cathode/electrolyte interfaces.It’s a critical issue for the successful commercialization of solid oxide fuel cells (SOFCs) to achieve long-term thermal stability without significant performance degradation. Current work reports a cost-competitive and scalable method for modifying porous Gadolinia doped ceria (GDC) barrier layers, to obtain an almost-dense, sintering-active, and Sr-blocking cathode/electrolyte interface, by growing nanoparticles in-situ on porous surfaces. The cell performance only deteriorates by ~0.5% after 20 times thermal cycles as the temperature fluctuated between 200 and 750 ℃, which is more prominent enhancement than ~16% for pristine cell, and exhibits higher initial performance. The hydrothermal modified symmetric cell shows ~60% polarization resistance decrease and well-attached cathode/electrolyte interfaces after ~1200 hours of operation, exhibiting excellent stability while the pristine cell interfaces peeled off. The performance improvements and prolonged operation mechanisms are discussed and mainly attributed to the almost-dense barrier layer and robust cathode/electrolyte interfaces.