Abstract:La0.6Sr0.4CoO3 (LSC) coatings with a thickness of 50-100 µm were deposited on Fe-25Cr ferritic stainless steel (DIN 50049) via screen printing. The required suspension had been prepared using fine LSC powders synthesised using EDTA gel processes. In its bulk form, the LSC consisted entirely of the rhombohedral phase with space group R-3c, and it exhibited high electrical conductivity (~144 S·cm-1). LSC-coated steel was oxidised in air at 1073 K, i.e., under conditions corresponding to SOFC cathode operation, for times of up to 144 h. The in situ electrical resistance of the steel/La0.6Sr0.4CoO3 layered system during oxidation was measured. The products formed on the samples after the oxidation reaction resulting from exposure to the corrosive medium were investigated using XRD, SEM-EDS, and TEM-SAD. The microstructural, nanostructural, phase, and chemical analysis of films was performed with a focus on the film/substrate interface. It was determined that the LSC coating interacts with the oxidised steel in the applied conditions, and a multi-layer interfacial zone is formed. Detailed TEM-SAD observations indicated the formation of a main layer consisting of SrCrO4, which was the reaction product of (La,Sr)CoO3, and the Cr2O3 scale formed on the metal surface. The formation of the SrCrO4 phase resulted in improved electrical conductivity of the investigated metal/ceramics layered composite material, as demonstrated by the low area-specific resistance values of 5 mΩ·cm2, thus making it potentially useful as a SOFC interconnect material operating at the tested temperature. In addition, the evaporation rate of chromium measured for the uncoated steel and the steel/La0.6Sr0.4CoO3 layered system likewise indicates that the coating is capable of acting as an effective barrier against the formation of volatile compounds of chromium.

Oxidation and electrical behavior of Ni-Mn3O4-La2O3-coated SOFC interconnect steel

High-entropy FeCoNiMnCu alloy coating on ferritic stainless steel for solid oxide fuel cell interconnects

CrxN/Mn1.7Cu1.3 coating on ferritic stainless steel for solid oxide fuel cell interconnects

Oxidation and electrical behavior of AISI 430 steel coated with Ni–P–TiO2–ZrO2 composite for SOFC interconnect application

Characterization of La0.8Sr0.2Co0.5Mn0.5O3-δ Coating on Alloy Interconnect in SOFC

Evaluation of Protective La0.67Sr0.33MnO3–δ Coatings on Various Stainless Steels Used for Solid Oxide Fuel Cell Interconnects

The Preparation and Properties of Ti(Nb)-Si-C Coating on the Pre-Oxidized Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

Oxidation and electrical properties of nanostructured CeO 2 –Ni coating on solid oxide fuel cell interconnects

The electrical property of MnCo2O4 and its application for SUS 430 metallic interconnect

Ni–Co/ZrO2 Composite Coatings via Electroless Plating on Crofer 22APU for SOFC Interconnect Applications: Oxidation and Chromium Vaporization Behavior

Thermal conversion and evolution behavior of surface scale on SOFC interconnect steel with sputtered FeCoNi coating

Physicochemical Properties of (La,Sr)CoO3 Thick Films on Fe-25Cr Steel under Exposure to SOFC Cathode Operating Conditions

Supersonic spray derived Cu–Co oxide coating on SUS441 to protect the metallic interconnect and to increase stability of SOFC cathode

Fabrication of Mn–Co Alloys Electrodeposited on AISI 430 Ferritic Stainless Steel for SOFC Interconnect Applications

Effect of MnCoNiFeCu Alloy on Oxidation Behavior and Electrical Performance of AISI 441 for SOFC Interconnect Application

Cu doped Mn-Co spinel protective coating on ferritic stainless steels for SOFC interconnect applications

Fe doped Ni–Co alloy by electroplating as protective coating for solid oxide fuel cell interconnect application

Effect of Cu on the diffusion behavior and electrical properties of Ni-Co conversion coating for metallic interconnects in solid oxide fuel cells

Characterization of the conductive protection layers on alloy interconnect for SOFC

High Temperature Oxidation Behavior of SUS430 SOFC Interconnects with Mn-Co Spinel Coating in Air

Sputtered Fe1·5CoNi0.5 coating: An improved protective coating for SOFC interconnect applications