Abstract:AISI 430 stainless steel is used for interconnects in solid oxide fuel cells (SOFCs). One of the main problems with this steel is the formation of chromia scales during oxidation at high temperature and thus increasing electrical resistance. In order to solve such problems, a protective and conductive coating layer can be applied on interconnects. In this study, AISI 430 steel was coated by Ni–P–TiO2–ZrO2 composite coating. To evaluate the oxidation behavior, isothermal and cyclic oxidation tests were used at 800 °C. Area specific resistances (ASR) of uncoated and coated samples were also compared as a function of time during oxidation at 800 °C. Chemical composition and surface morphology of the samples were examined before and after oxidation by Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD). In isothermal and cyclic oxidation tests, coated samples showed lower weight gain due to the formation of Ni2P2O7, Ni3P2O8, and NiFe2O4 spinel. This spinel prevented outward Cr diffusion, and improved the oxidation resistance of the AISI 430 stainless steel substrate. The obtained result by cyclic oxidation revealed that the coated substrates were resistant against cracking and spallation. Also, the results showed that the formation of Ni2P2O7, Ni3P2O8, and NiFe2O4 spinel and also the presence of TiO2 and ZrO2 caused ASR reduction. ASR of Ni–P–TiO2–ZrO2-coated specimens after 300 h of oxidation at 800 ºC (14.21 mΩ cm2) was lower than the uncoated specimens (41.84 mΩ m2) after the same time of oxidation.

High temperature oxidation and chromium volatilisation of AISI 430 stainless steel coated by Mn-Co and Mn-Co-Cu oxides for SOFC interconnect application

Development of Annealed Mn–Co and Mn–Co–Cu Coated AISI 430 Stainless Steels for SOFC Interconnect Application

Fabrication of Mn–Co Alloys Electrodeposited on AISI 430 Ferritic Stainless Steel for SOFC Interconnect Applications

Oxidation and electrical behavior of AISI 430 steel coated with Ni–P–TiO2–ZrO2 composite for SOFC interconnect application

High Temperature Oxidation Behavior of SUS430 SOFC Interconnects with Mn-Co Spinel Coating in Air

High-entropy FeCoNiMnCu alloy coating on ferritic stainless steel for solid oxide fuel cell interconnects

Experimental Investigation of the Initial Stage of the Oxidation Mechanism of Co Coating for Solid Oxide Fuel Cell Interconnects at 650 °C

Characterization of La0.8Sr0.2Co0.5Mn0.5O3-δ Coating on Alloy Interconnect in SOFC

Effect of MnCoNiFeCu Alloy on Oxidation Behavior and Electrical Performance of AISI 441 for SOFC Interconnect Application

Ni–Co/ZrO2 Composite Coatings via Electroless Plating on Crofer 22APU for SOFC Interconnect Applications: Oxidation and Chromium Vaporization Behavior

Development and Application of HVOF Sprayed Spinel Protective Coating for SOFC Interconnects

Performance of stainless steel interconnects with (Mn,Co)3O4-Based coating for solid oxide electrolysis

Supersonic spray derived Cu–Co oxide coating on SUS441 to protect the metallic interconnect and to increase stability of SOFC cathode

Performance and In-Situ Densification of Mn-Co Spinel Coating on SUS430/441 Interconnect by Spraying Method

The Preparation and Properties of Ti(Nb)-Si-C Coating on the Pre-Oxidized Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

Effects of Temperature and Water Vapour on Cr-Species Volatilisation, Oxidation and Scale Adhesion of a Type 409 L Stainless Steel for Application as Interconnect of Low Temperature Solid Oxide Fuel Cells

Evaluation of SUS430 with Mn-Co Coating As SOFC Interconnect in Reducing Atmosphere

Corrosion Behaviour of AISI 430 Stainless Steel in O2-40%H2O at 800 °C

CrxN/Mn1.7Cu1.3 coating on ferritic stainless steel for solid oxide fuel cell interconnects

Oxidation and electrical behavior of Ni-Mn3O4-La2O3-coated SOFC interconnect steel

Effect of bias voltage on high-temperature oxidation resistance and electrical properties of Mn-Co coating with metal interconnects for solid oxide fuel cell