Abstract:To lower deposition temperature and reduce thermal mismatch induced stress, heteroepitaxial growth of single-crystalline 3C–SiC on 150mm Si wafers was investigated at 1000°C using alternating supply epitaxy. The growth was performed in a hot-wall low-pressure chemical vapor deposition reactor, with silane and acetylene being employed as precursors. To avoid contamination of Si substrate, the reactor was filled in with oxygen to grow silicon dioxide, and then this thin oxide layer was etched away by silane, followed by a carbonization step performed at 750°C before the temperature was ramped up to 1000°C to start the growth of SiC. Microstructure analyses demonstrated that single-crystalline 3C–SiC is epitaxially grown on Si substrate and the film quality is improved as thickness increases. The growth rate varied from 0.44 to 0.76 ±0.02nm/cycle by adjusting the supply volume of SiH4 and C2H2. The thickness nonuniformity across wafer was controlled with ±1%. For a prime grade 150mm virgin Si(100) wafer, the bow increased from 2.1 to 3.1μm after 960nm SiC film was deposited. The SiC films are naturally n type conductivity as characterized by the hot-probe technique.

Growth characteristics of C60 films on fluorophlogopite and silicon substrates

EPITAXIAL GROWTH OF (0001)ORIENTED 6H-Sic FILMS ON Si(111) SUBSTRATE BY ORGANIC SOL-GEL FILM ANNEALING

Growth of Crystalline SiC Film Free of Cavities by Heating PS/silica Sol-Gel Coatings on Si (111) Substrate

Growth Of C-60 Single Crystal Films On Metal Substrates

Growth and Mechanical Properties of Amorphous and Nanostructured SiC films

Optimal temperature of crystallization and photoluminescence of SiC/Si (100) film prepared by pulsed ArF excimer laser deposition

Sb Mediated C-60 Film Growth on Mica, Si, and Glass Substrates

Growth of C 60 (111) Single Crystalline Thin Film on Ni 3 Co(111) Substrate

Influence of the partial pressure of ethene on the crystallinity of 3C-SiC films grown on Si(111) by chemical vapor deposition

Film Growth And Surface Reactions Of C-60 On Si(100)H(2x1)

Growth of Poly-Crystalline Si Films on Flexible Substrate by Hot Wire Chemical Vapor Deposition

Effect of C/Si Ratio on the Characteristics of 3C-Sic Films Deposited on Si(100) Base on the Four-Step Non-Cooling Process

Low-Temperature Synthesis of C-60 Thin Films by Ionized Cluster Beam Deposition Technique

Sb induced compact-fractal-compact growth transition of C60 films

Growth of Si-C-H film by RF plasma enhanced chemical vapor deposition

Growth of High-Quality C60(111) Single Crystalline Film on Ni3Co(111) Surface

Film Growth and Surface Reactions Ofc60onsi(100)h

Influence of C_2H_4 on the Properties of Amorphous Silicon Film Grown by Chemical Vapor Deposition

Growing high-quality C60 films by using Sb buffer layer

STUDY ON GROWTH OF C 60 MOLECULES ON GaAs(001) SUBSTRATE BY SCANNING TUNNELING MICROSCOPY

Growth of 3C–SiC on 150-mm Si(100) substrates by alternating supply epitaxy at 1000°C