Abstract:Magnesium aluminate (MgAl2O4) spinel has grasped considerable attention in high-temperature application by right of its excellent properties. However, the poor sintering behavior of MgAl2O4 is detrimental to its further development. In the present work, the application of isostructural heterogeneous nucleation method provides a novel idea for optimizing the sintering behavior of refractory materials. A series of (1-x)MgAl2O4-xMg2TiO4 (x = 0, 0.02, 0.04, 0.06, 0.08, and 0.1) spinel solid solutions with a present ration of components were fabricated from light calcined magnesia, reactive alumina and pre-preparation Mg2TiO4. The effect of Mg2TiO4 heterogeneous nucleating agent on the crystalline phase, densification, and microstructure evolution of MgAl2O4–Mg2TiO4 spinel solid solutions was studied. The XRD, XPS, and EDS results showed that Mg2TiO4 entered the lattice of MgAl2O4 to form a spinel solid solution, and the heterovalent substitution process was identified, where Ti4+ and Mg2+ ions of larger radius in the Mg2TiO4 replaced the Al3+ of smaller radius in the MgAl2O4. For the sample at x = 0.08, the spinel solid solutions exhibited the optimized densification with a relative density of 93.3%, an apparent porosity of 1.2%, and a compressive strength of 84.5 MPa. A significant increase in densification was related to the lattice distortion induced by ion size mismatch during the heterovalent substitution, thus accelerating the diffusion rate of Mg2+ and Al3+ ions in the spinelisation state. Moreover, the solid solubility content of Ti4+ in the MgAl2O4–Mg2TiO4 spinel solid solutions had a significant effect on the grain morphologies. The Mg2TiO4 heterogeneous nucleating agent significantly increased the spinelisation rate of MgAl2O4 spinel with negligible effect on densification.

Effect of the citrate sol–gel synthesis on the formation of MgAl2O4 ultrafine powder

The low temperature preparation of nanocrystalline MgAl2O4 spinel by citrate sol–gel process

Synthesis of O′-SiAlON ultrafine powder

Synthesis of Nano-Alumina Hydroxide Sol Using Sol-gel Method

Synthesis of ultrafine MgAl2O4 powders by sol-gel auto ignition

Effect of Synthetic Parameters on Synthesis of Magnesium Aluminum Spinels

Effects of chelation reactions between metal alkoxide and acetylacetone on the preparation of MgAl2O4 powders by sol-gel process

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Preparation and Characterization of Cordierite Powder Via Tween-80 Modified Citrate Sol-Gel Method

SYNTHESIS OF NANOMETER MAGNESIA BY SOL- GEL METHOD

Synthesis of MgAl2O4Spinel Nanometer Powder Via Biology Polysaccharide Assisted Sol-Gel Process

Sintering behavior and microstructure of (1-x)MgAl2O4-xMg2TiO4 spinel solid solutions prepared by isostructural heterogeneous nucleation

Preparation and Characterization of Citrate Sol-Gel Derived Ba(Zr,Ti)O3 Ceramics with Al2O3 Addition

Effect of different MgO/Al2O3 ratios on microstructural densification, sintering process and mechanical property of MgAl2O4 materials

The low temperature fabrication of nanocrystalline MgAl2O4 spinel aerogel by a non-alkoxide sol-gel route

Preparation and Crystallization of Si-Al Gel

Preparation of nanosized CoAl2O4 powders by sol–gel and sol–gel-hydrothermal methods

Preparation of Alumina Ultrafine Powders Through Acrylamide, Starch and Glutaric Dialdehyde Mediated Sol–gel Method

Preparation of Nanocrystalline Mullite Contained Microspheres by Sol-gel Process in Oil-in-Water Emulsion

Effect of the Way of Water Addition on the Morphology of Nano-Sized Al2O3 Powders Prepared by Sol-Gel Method

Effect of Magnesium Oxide on Preparation of Mullite Fibers Via Sol-Gel Method