Abstract:Ordered mesoporous, crystalline MgTa2O6 thin films with a mesoscopic nanoarchitecture were synthesized by evaporation-induced self-assembly (EISA) in combination with a sol-gel procedure. Utilization of novel templates, namely the block copolymers KLE (poly(ethylene-co-butylene)-b-poly(ethylene oxide)) and PIB6000 (CH3C(CH3)(2)(CH2C(CH3)(2))(107)CH2C(CH3)(2)C6H4O(CH2CH2O)(100)H), was the key to achieving a stable ordered mesoporous structure even upon crystallization of MgTa2O6 within the mesopore walls. The effect of the calcination temperature on the ability of the mesoporous films to assist the photodegradation of rhodamine B in water was studied. As a result, two maxima in the photocatalytic activity were identified in the calcination temperature range of 550-850 degrees C, peaking at 700 degrees C and 790 degrees C, and the origin of this was investigated by using temperature-dependent X-ray scattering. Optimal activity was obtained when the mesoporous film was heated to 790 degrees C; at this temperature, crystallinity was significantly high, with MgTa2O6 nanocrystals of 1.6 nm in size (averaged over all reflections), and an ordered mesoporous structure was maintained. When considering the turnover frequency of such photocatalysts, the optimized activity of the present nanoarchitectured MgTa2O6 thin film was ca. four times that of analogous anatase TiO2 films with ordered mesopores. Our study demonstrated that high crystallinity and well-developed mesoporosity have to be achieved in order to optimize the physicochemical performance of mesoporous metal-oxide films.

Synthesis of MgTa2O6 Nano-Powders by Citrate Sol–gel Method

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Preparation of LiTaO 3 nanoparticles by a sol–gel route

Preparation of LiTaO<sub>3</sub> nanoparticles by a sol–gel route

Mesoporous MgTa 2o 6 thin films with enhanced photocatalytic activity: On the interplay between crystallinity and mesostructure

pH control on preparation of nano-TiO_2 by gel-sol process

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Synthesis of Nanopowders of Ba(Ti0.8Zr0.2)O3

Citric Acid Gel Method Synthesis, Characterization And Dielectric Properties Of Single-Phase Bati4o9

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Study of the synthetic process of CaBi2Ta2O9 powder by the molten‐salt method

Low temperature synthesis of (Pb,La)(Zr,Sn,Ti)O 3 powders by citrate process

Preparation of pure MgTiO3 powders and the effect of the ZnNb2O6-dope onto the property of MgTiO3-based ceramics

Synthesis of Nanocrystalline 0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub> Powder by a Citrate Method

Synthesis and Characterization of BaTiO3 Nanopowders Via Solvothermal Method

Synthesis of Aluminum Titanate Solid Solution by Solid State Reaction of Fine Commercial Al2o3, Tio2 and Mgo Powders

The low temperature preparation of nanocrystalline MgAl2O4 spinel by citrate sol–gel process

Synthesis of ZnTiO3 Ceramic Powders by Sol-Gel Method

Characterization of ZnTiO 3 powders prepared by sol-gel process

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature