Abstract:In the present work, effects of ZrC addition (10, 15, 20, 25 vol%) on microstructure and mechanical properties of ZTA20mol% (Zirconia-20mol% Toughened Alumina) ceramic composites were investigated. Samples were prepared by Hot Pressing Sintering (HP) at 1 600 ℃ and 30 MPa for a soaking time of 2 hours. Microstructures were characterized by XRD, Raman, SEM and TEM. XRD and Raman spectra results revealed that only ZrC, α-Al2O3 and ZrO2 were detected for all composites, indicating that these ceramic composites had excellent chemical compatibilities. SEM images showed refined microstructure was obtained, and the fracture surfaces exhibited a mixed process of transgranular and intergranular fracture. According to the TEM observations, some nano-sized ZrC particles dispersed inside Al2O3 grains and formed an intra/inter-type nanostructure. The relative densities and Vickers hardness were inversely proportional to ZrC content, which gradually decreased from 98.24% to 94.89%, from 1 847 to 1 691 HV1, respectively. Flexural strength and fracture toughness were tested by three-point bending method and single-edge notched beam method, respectively. The fracture toughness increased at first and then decreased with ZrC content increased from 0 to 25 vol%. The maximum value was 11.23 MPa.m1/2 with 20 vol% ZrC addition, with an enhancement of 51% compared to the undoped ZTA mixture. The flexural strength, with a maximum of 1 121 MPa without ZrC addition and decreased to 645MPa with ZrC-10(vol%) addition, then increased monotonously to 1084 MPa as the ZrC content increased from 10 to 25 vol%.

Study on Ceramic Tool Material with Nano-scale Zirconia Toughening Alumina Matrix

Coated-ZrO2 Toughening Al2O3 Matrix Ceramics

The Effect of Nano-Al2O3 on Sintering Behavior and Mechanical Property of ZrO2 Ceramics

The Effect of Nano-Al<sub>2</sub>O<sub>3</sub> on Sintering Behavior and Mechanical Property of ZrO<sub>2</sub> Ceramics

Synthesis of zirconia nanoparticles on carbon nanotubes and their potential for enhancing the fracture toughness of alumina ceramics

Effects of ZrC content on the microstructure and mechanical property of ZrC/ZTA composites consolidated by hot pressing

Microstructure and mechanical properties of dense ZTA ceramics with high Cr2O3 solution

Optimization of sintering parameters for fabrication of Al2O3/TiN/TiC micro-nano-composite ceramic tool material based on microstructure evolution simulation

A novel method for fabricating brick-mortar structured alumina-zirconia ceramics with high toughness

Fabrication and Mechanical Properties of Homogeneous Zirconia Toughened Alumina Ceramics Via Cyclic Solution Infiltration and in Situ Precipitation

Preparation, mechanical properties, and toughening mechanisms of SiCw/SiCp‐reinforced zirconia‐toughened alumina ceramics

Microstructure, mechanical properties, friction and wear performance, and cytotoxicity of additively manufactured zirconia-toughened alumina for dental applications

Alumina ceramic tool material with enhanced properties through the addition of bionic prepared nano SiC@graphene

Effects of Sr2Nb2O7 additive on microstructure and mechanical properties of 3Y–TZP/Al2O3 ceramics

Effects of Zircon Additive on the Properties of 95-Alumina Ceramic

Strengthening of porous Al2O3 ceramics through nanoparticle addition

SiC and ZrN Nano-Particulate Reinforced AlON Composites: Preparation, Mechanical Properties and Toughening Mechanisms

Microstructure and Toughening Mechanisms of Al2O3/(W, Ti)C/graphene Composite Ceramic Tool Material

Surface Modification of Graphene Oxide and Its Strengthening and Toughening Mechanism for Alumina-Based Ceramic Materials

Enhanced Mechanical Properties in Ceramic Multilayer Composites Through Integrating Crystallographic Texture and Second-Phase Toughening

Study on the mechanical properties and microstructure of Al2O3/nano-SiC multiphase ceramics