Abstract:Binder jetting additive manufacturing (BJAM), a combination of liquid binder and solid powders, was widely utilized to fabricate complex–structured alumina (Al 2 O 3 ) ceramic cores. However, the high porosity, high brittleness and low mechanical strength of Al2O3 ceramics generally limit their industrial applications. To balance the contradiction between porosity and bending strength and improve the fracture toughness of Al2O3 ceramic core, sodium silicate (Na2O·3.2SiO2) solution and 5 mol% yttrium oxide stabilized zirconia (5YSZ) nanopowders were selected as densifier and toughening phase in this study. By means of the vacuum infiltration and sintering process, the effects of Na2O·3.2SiO2 contents, sintering temperatures and 5YSZ amounts on porosity, bending strength, and fracture toughness of Al2O3 ceramic were systematically investigated. Results show that the porosity and fracture stress of Al 2 O 3 infiltrated with 30 wt.% Na 2 O·3.2SiO 2 solution sintered at 1550 °C reached 21.4±1.1% and about 52.7 MPa, respectively. When the amounts of 5YSZ in 30 wt.% Na 2 O·3.2SiO 2 solution were increased from 0 wt.% to 6 wt.% and the sintering temperatures were varied from 1400 °C to 1550 °C, the fracture toughness of Al 2 O 3 ceramic gradually enhanced to the maximum value of 2.8185±0.071 MPa/m 1/2 obtained at 4 wt.% 5YSZ and 1550 °C, which was increased by 87.44% compared with the infiltrated sample without 5YSZ. Therefore, using BJAM technology to fabricate a strong–tough Al 2 O 3 ceramic cores for the turbine blades casting could realize short process and efficient preparation of the ceramic cores, which had a great theoretical foundation and application potential in the casting field.

Strengthening of porous Al2O3 ceramics through nanoparticle addition

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

TOUGHENING AND STRENGTHENING OF Al_2O_3 CERAMICS THROUGH NANO-Al_2O_3 ADDITION

Effect of Type and Content of Pore-forming Agents on Properties of Porous Alumina Membrane Support

Effect of Particle Size Distribution of Raw Powders on Pore Size Distribution and Bending Strength of Al2o3 Microfiltration Membrane Supports

The Effect of Nano-Al2O3 on Sintering Behavior and Mechanical Property of ZrO2 Ceramics

The Effect of Nano-Al<sub>2</sub>O<sub>3</sub> on Sintering Behavior and Mechanical Property of ZrO<sub>2</sub> Ceramics

Synthesis of zirconia nanoparticles on carbon nanotubes and their potential for enhancing the fracture toughness of alumina ceramics

Fabrication and mechanical properties of nacre-like alumina with addition of silicon nitride

Microstructure and Mechanical Properties of Porous Alumina Ceramics Fabricated by the Decomposition of Aluminum Hydroxide

Study on the mechanical properties and microstructure of Al2O3/nano-SiC multiphase ceramics

Nanoscale toughening of low carbon Al2O3‐C refractories by means of SiCnw/Al2O3 composite reinforcement

Effect of sodium silicate solution combined yttrium oxide stabilized zirconia nanopowders on the properties of alumina ceramics fabricated by binder jetting additive manufacturing

Coated-ZrO2 Toughening Al2O3 Matrix Ceramics

In Situ Growth of Elongated Al2O3 Grains Induced by Al Nanoparticles

Surface Modification of Graphene Oxide and Its Strengthening and Toughening Mechanism for Alumina-Based Ceramic Materials

SiC and ZrN Nano-Particulate Reinforced AlON Composites: Preparation, Mechanical Properties and Toughening Mechanisms

Synthesis, Evaluation And Characterization Of Alumina Ceramics With Elongated Grains

Effect of zirconia sol on the microstructure and properties of Al2O3-based ceramic fabricated from natural bauxite

Enhanced properties of nanocrystalline alumina ceramic with compressive prestress and coherently aligned nanograins

SiC Nanoparticles Strengthened Alumina Ceramics Prepared by Extrusion Printing