Enhanced oxidation resistance and thermal shock resistance of low-carbon Al 2 O 3 –C refractories with nano-BN: A synergistic of mullitization behavior
Yixin Luo,Xing Wang,Zhenglong Liu,Chao Yu,Chengji Deng,Jun Ding
DOI: https://doi.org/10.1016/j.jallcom.2023.172937
IF: 6.2
2023-12-02
Journal of Alloys and Compounds
Abstract:The thermal shock stability and oxidation resistance of Al 2 O 3 –C refractories are of critical importance for iron and steel making processes. In rapid and repeated thermal shock environments, materials require excellent thermal shock stability and oxidation resistance. In this study, nano-BN synthesized was used to introduce Al 2 O 3 –C refractories, as well as in evaluating the oxidation resistance and thermal shock resistance of the materials. The results shows that B 2 O 3 was formed rapidly in the refractory containing nano-BN under low temperature oxidation, hence, it led to the decrease of the formation temperature of the dense insulating layer. As a result, the low temperature oxidation resistance of the material was improved. Simultaneously, at high temperatures, Al 18 B 4 O 33 enhanced the formation kinetics of Al 6 Si 2 O 13 by providing epitaxial nucleation sites, forming a synergistic structure of Al 18 B 4 O 33 and Al 6 Si 2 O 13. This change promoted the connection of the oxide layer, thereby greatly improving the oxidation resistance of the material. Moreover, the introduction of nano-BN was beneficial for improving the thermal shock stability of Al 2 O 3 –C refractories.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering