Abstract:Ultralong Si 3 N 4 nanowires (NWs) were successfully synthesized with size controlled in N 2 gas by using an efficient method. The diameters of the Si 3 N 4 NWs increased when the flow rate of N 2 gas increased, with average diameters of 290 nm from flow rates of 100 ml/min, 343 nm from flow rates of 200 ml/min and 425 nm from flow rates of 400 ml/min. Young’s modulus was found to rely strongly on the diameters of the Si 3 N 4 NWs, decreasing from approximately 526.0 GPa to 321.9 GPa; as the diameters increased from 360 nm to 960 nm. These findings provide a promising method for tailoring these mechanical properties of the NWs in a controlled manner over a wide range of Young’s modulus values. Vapour-liquid-solid (VLS) mechanisms were used to model the growth of Si 3 N 4 NWs on the inner wall of an alumina crucible and on the surface of the powder mixture. Alumina may be an effective mediator of NW growth that plays an important role in controlling the concentrations of Si-containing reactants to support the growth of NWs on the inner wall of the alumina crucible. This approach offers a valuable means for preparing ultralong Si 3 N 4 NWs doped with Al with unique properties.

Synthesis of Α Silicon Nitride Single-Crystalline Nanowires by Nitriding Cryomilled Nanocrystalline Silicon Powder

Ultrafast growth of single-crystalline Si nanowires

Mass Production of Α-Silicon Nitride Single-crystalline Nanowires

Synthesis and Characterization of Α-Phase Silicon Nitride Powders by Direct Nitridation

Direct Synthesis of Α-Silicon Nitride Nanowires from Silicon Monoxide on Alumina

Synthesis of Si 3 N 4 Nanowires by Catalyst‐free Nitridation of (si + SiO 2 ) Mixture

Synthesis and Characterization of Amorphous Silicon Nitride Nanoparticals and α‐Silicon Nitride Nanowires

Bulk Synthesis of Long Silicon Nitride Nanowires on Silicon Wafer

Synthesis and Characterization of Several alpha-Silicon Nitride Nanostructures

Long Silicon Nitride Nanowires Synthesized in a Simple Route

Fabrication Of Alpha-Si3n4 Nanobelts Assembled By Si3n4 Microcrystals On The Nanowires Via Crystallization Of Amorphous Si3n4 Powders

Facile synthesis of silicon nitride nanowires with flexible mechanical properties and with diameters controlled by flow rate

A Novel Approach To Silicon-Nanowire-Assisted Growth Of High-Purity, Single-Crystalline Beta-Si3n4 Nanowires

Tiny SiO2 nano-wires synthesized on Si (111) wafer

Phase-controlled Synthesis of Nickel Silicide Nanostructures

Large Scale Synthesis of Si3N4@SiOx Core-Shell Structure Nanowires by Direct Nitridation

Synthesis And Growth Mechanism Of Silicon Nitride Nanostructures

Synthesis of Si 3 N 4 powder with tunable α/β-Si 3 N 4 content from waste silica fume using carbothermal reduction nitridation

Fabrication of α-Si3N4 nanobelts assembled by Si3N4 microcrystals on the nanowires via crystallization of amorphous Si3N4 powders

Novel, Low-Cost Solid-Liquid-solid Process for the Synthesis of Α-Si3n4 Nanowires at Lower Temperatures and Their Luminescence Properties

One-step Synthesis Route of the Aligned and Non-Aligned Single Crystalline Α-Si3n4 Nanowires