Abstract:Silicon nanowires with narrowly distributed diameters of 20-30 nm have been fabricated by chemical vapor deposition on an anodized aluminum oxide (AAO) substrate. The first-order and second-order Raman scatterings of the silicon nanowires have been studied in a temperature range from 123 to 633 K. Both of the first-order and second-order Raman peaks were found to shift and broaden with increasing temperature. The experimental results were analyzed by combining the phonon confinement effect, anharmonic phonon processes and lattice stress effect. It was found that the intensities of the first-order and second-order Raman bands have different dependences on temperature. The value of relative intensities I(2TA)int/I(2TO)int for silicon nanowires was found to be larger than that of bulk silicon, and increase with rising measurement temperature. We ascribe this phenomenon to the participation of phonons with a large wave vector value of Raman scattering caused by both the phonon confinement effect and the temperature effect.

Synthesis and Raman Spectra of Si-Nanowires

Ultrafast growth of single-crystalline Si nanowires

Raman Spectrum of Array-Ordered Crystalline Silicon Nanowires

Crystallization and Raman Shift of Array-Orderly Silicon Nanowires after Annealing at High Temperature

Array-orderly single crystalline silicon nano-wires

Infrared Spectra of Silicon Nanowires

Tiny SiO2 nano-wires synthesized on Si (111) wafer

Sulfide-assisted Growth of Silicon Nano-Wires by Thermal Evaporation of Sulfur Powders

Tiny silicon nano-wires synthesis on silicon wafers

Tiny SiO2 nano-wires synthesized on Si (1 1 1 ) wafer

Temperature-dependent Raman Scattering of Silicon Nanowires.

Silicon Nano-Wires Fabricated by Thermal Evaporation of Silicon Wafer

Silicon Nano-Wires Fabricated by a Novel Thermal Evaporation of Zinc Sulfide

A Novel Sulfide-Assisted Growth of Silicon Nano-Wires

Silicon Quantum-Wires Arrays Synthesized by Chemical Vapor Deposition and Its Micro-Structural Properties

Silicon Nanowire Synthesis by Chemical Vapor Deposition

Silicon nanowires fabricated by thermal evaporation of silicon monoxide

Synthesis and characterization of well-aligned quantum silicon nanowires arrays

Raman spectroscopy and field electron emission properties of aligned silicon nanowire arrays

Ordered Arrays of High-Quality Single-Crystalline Α-Si3n4 Nanowires: Synthesis, Properties and Applications

Crystallization and Disappearance of Defects of the Annealed Silicon Nanowires