Abstract:Preparing high-quality AlN films at low temperatures is always highly demanded in plenty of application-fields, despite the high temperature is always necessary to enable the AlN crystallization. Therefore, improving the structural properties at low temperature is still challenging in the field. In the present work, the metal organic chemical vapor deposition (MOCVD) grown AlN nucleation layer is employed to improve the crystallinity and morphology of sputtered AlN on 6-inch Si (111) substrate at the temperature even as low as 100°C where it is not principally possible to achieve the crystallization of sputtered AlN. When compared with the as-sputtered AlN prepared even at 650°C, it is found that the full width at half maximum (FWHM) of AlN (002) X-ray rocking curves is intensively decreased to 0.96° from 1.61°, and such a reduction indicates that the screw dislocation density is decreased from 7.31×1010 down to 2.14×1010/cm2. In addition to the crystallinity, the morphology is also obviously improved that the root-mean-square (RMS) roughness is reduced from 4.99 nm down to 0.83 nm in a scanned area of 3×3 μm2 through introducing AlN nucleation. Therefore, such a combination highlights the contribution of AlN nucleation grown by MOCVD in improving the structural properties of low-temperature sputtered AlN layer which is compatible with the manufacturing of Si integrated circuits.

Cryogenic microwave performance of silicon nitride and amorphous silicon deposited using low-temperature ICPCVD

Cryogenic Microwave Performance of Silicon Nitride and Amorphous Silicon Deposited Using Low-Temperature ICPCVD

Material properties of a low contraction and resistivity silicon-aluminum composite for cryogenic detectors

Annealing reduces Si$_3$N$_4$ microwave-frequency dielectric loss in superconducting resonators

Enhanced Mechanical Properties of SiC/Al Composites at Cryogenic Temperatures

Annealing reduces microwave-frequency dielectric loss in superconducting resonators

Research of Mechanical and Thermal Properties of SiC at Cryogenic Temperatures

Low-loss Si-based Dielectrics for High Frequency Components of Superconducting Detectors

A Planar Al-Si Schottky Barrier Metal-Oxide-Semiconductor Field Effect Transistor Operated at Cryogenic Temperatures

Low-temperature characteristics and gate leakage mechanisms of LPCVD-SiN<i>x</i>/AlGaN/GaN MIS-HEMTs

Low-Temperature Materials And Thin Film Transistors For Flexible Electronics

Cryogenic GaN/AlGaN HEMT ICs and Fabrication Probability of Monolithic Sensor of Super- and Semiconductor Devices

Preparation and Dielectric Properties of SiC-AlN Solid Solutions

PREPARATION AND MICROWAVE ATTENUATION PERFORMANCE OF AIN - SiC COMPOSITES

Low Temperature Sintering and Performance of Aluminum Nitride/Borosilicate Glass

Low firing temperature ceramic material for high frequency multilayer chip inductors

Highly Temperature-Stable Carbon Nanotube Transistors and Gigahertz Integrated Circuits for Cryogenic Electronics

Wafer-Scale Characterization of a Superconductor Integrated Circuit Fabrication Process, Using a Cryogenic Wafer Prober

A Very Low Temperature Single Crystal Germanium Growth Process on Insulating Substrate Using Ni-Induced Lateral Crystallization for Three-Dimensional Integrated Circuits

A liquid nitrogen cooled superconducting transition edge sensor with ultra-high responsivity and GHz operation speeds

Improving the structural performance of low-temperature sputtered AlN on silicon substrate