Abstract:The Al2O3/SiO2–B2O3–Al2O3–Na2O glass/Al2O3 joints reinforced cooperatively by glass matrix and in-situ Al4B2O9 whiskers were obtained via a low-melting borosilicate glass braze. The composition of glass seam transformed from SiO2–B2O3–Na2O to SiO2–B2O3–Al2O3–Na2O due to continuous diffusion and dissolution of Al2O3. An appropriate amount of [AlO4] units introduced into the glass braze played a vital role in strengthening the glass network structure resulting to considerably improved mechanical strength of the glass seam. Meanwhile, plenty of in-situ Al4B2O9 whiskers growing from the Al2O3/glass braze interface to the center of glass seam in various directions generated. Three-dimensional crisscross structures were fabricated at the Al2O3/glass braze interface domains, where were enhanced by crack-bridging and pull-out effect of the whiskers. Generally, ascribed to the cooperative reinforcement of the glass matrix in the seam and in-situ Al4B2O9 whiskers at Al2O3/glass braze interface domains through reactions of Al2O3 and borosilicate glass braze, strength of the as-brazed joints was promoted prominently. The shear strength of the joints reached a maximum of 61 MPa brazed at 1050 °C for 60 min.

Two-step joining of reaction bonded silicon carbide (RBSC) using borosilicate glass

Joining of sintered SiC ceramics at a lower temperature using borosilicate glass with laser cladding Si modification layer

Research on Silicon-Glass Thermal Bonding with SiO2 Film Assist

Evaluation of Low-Temperature Glass Fillers and Joining of Reaction-Bonded Silicon Carbide Ceramics at Vacuum

Joining Pre-Oxidized Dense Si3N4 to Porous Si3N4 with Β-Spodumene Based Glass-Ceramic Interlayer

Joining of SiC ceramics using CaO-Al2O3-SiO2 (CAS) glass ceramics

Joining of SiC ceramics using CaO-Al<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> (CAS) glass ceramics

Microstructure, Mechanical Property and Bonding Mechanism of SiC Ceramic Joint Using a Novel Y2Si2O7/Mullite Glass-Ceramic Interlayer

Joining of Cf/SiC composites and Si<sub>3</sub>N<sub>4</sub> ceramic with Y<sub>2</sub>O<sub>3</sub>-Al<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> glass filler for high-temperature applications

Reaction forming of joints in silicon carbide ceramic materials

Joining high volume fraction SiC particle reinforced aluminum matrix composites using Bi2O3-B2O3-ZnO-BaO-Na2O glass

Joining Dense Si3N4 to Porous Si3N4 Using a Novel Glass-Ceramic Interlayer with Precipitated Β-Lialsi2o6/mg2sio4

Study on Joints of Reaction-Bonded Silicon Carbide Ceramic Materials

Microstructure and Properties of Porous Si3N4/Dense Si3N4 Joints Bonded Using RE–Si–Al–O–N (RE = Y or Yb) Glasses

Microstructure and mechanical properties of SiC joint using anorthite based glass-ceramic and first principles calculation of joint interface

Microstructure evolution and cooperative reinforcement mechanisms of Al2O3/Al2O3 joints brazed by low-melting borosilicate glass

Mechanical and electrical properties of reaction-formed joints in silicon carbide ceramic materials

Novel design of sapphire/spinel transparent ceramic joints with double glass interlayers by coating and bonding

Microstructure Evolution and Mechanical Properties of Porous Si3N4 and Dense Si3N4 Joints Bonded Using CaO–Li2O-Al2O3–SiO2 Glass-Ceramic

Crystallization Behaviour of 25bi2o3–75b2o3 Glass Braze and Strengthening Mechanism of Crystallization-Reinforced Sapphire/25bi2o3–75b2o3/sapphire Joints

Microstructure and Characterization of Interfacial Phases of Sapphire/sapphire Joint Bonded Using Bi2O3–B2O3–ZnO Glass