Abstract:A novel Y 3 Si 2 C 2 material was synthesized at a relatively low temperature (900 °C) using a molten salt method for the first time, and subsequently used as the joining material for carbon fiber reinforced SiC (C f /SiC) composites. The sound near-seamless joints with no obvious remaining interlayer were obtained at 1600 °C using an electric field-assisted sintering technique (FAST). During joining, a liquid phase was formed by the eutectic reaction among Y 3 Si 2 C 2 , γ (Y—C) phase, and SiC, followed by the precipitation of SiC particles. The presence of the liquid promoted the sintering of newly formed SiC particles, leading to their complete consolidation with the C f /SiC matrix. On the other hand, the excess of the liquid was pushed away from the joining area under the effect of a uniaxial pressure of 30 MPa, leading to the formation of the near-seamless joints. The highest shear strength ( τ ) of 17.2±2.9 MPa was obtained after being joined at 1600 °C for 10 min. The failure of the joints occurred in the C f /SiC matrix, indicating that the interface was stronger than that of the C f /SiC matrix. The formation of a near-seamless joint minimizes the mismatch of thermal expansion coefficients and also irradiation-induced swelling, suggesting that the proposed joining strategy can be potentially applied to SiC-based ceramic matrix composites (CMCs) for extreme environmental applications.

Joining of sintered SiC ceramics at a lower temperature using borosilicate glass with laser cladding Si modification layer

Two-step joining of reaction bonded silicon carbide (RBSC) using borosilicate glass

Femtosecond laser surface modification-based brazing of Si3N4 ceramics to 7A52 aluminum alloy

Joining of SiC ceramics using CaO-Al2O3-SiO2 (CAS) glass ceramics

Bonding strength enhancement of low temperature sintered SiC power module by femtosecond laser induced micro/nanostructures

Low-temperature joining of SiC ceramics by NITE phase using CaO-Al2O3-MgO-SiO2 glass as an additive combined with surface oxidation

Joining of SiC using CoFeCrNiCuTi high entropy alloy filler by electric current field assisted sintering

Joining of SiC ceramics by combining NITE-SiC interlayer and its thickness control

Microstructure and Properties of Porous Si3N4/Dense Si3N4 Joints Bonded Using RE–Si–Al–O–N (RE = Y or Yb) Glasses

Nanosecond laser-induced contact reactive brazing of Si3N4 ceramic to Al

Effects of the joining process on the microstructure and properties of liquid-phase-sintered SiC-SiC joints formed with Ti foil

Microstructure and Properties of Porous Si3N4/Dense Si3N4 Joints Bonded Using RE-Si-Al-O-N (RE = Y or Yb) Glasses

Ultrafast low-temperature near-seamless joining of Cf/SiC using a sacrificial Pr3Si2C2 filler via electric current field-assisted sintering technique

Low temperature seamless joining of SiC using a Ytterbium film

Microstructure Evolution and Mechanical Properties of 20%SiCp/Al Joint Prepared via Laser Welding

Microstructure and mechanical properties of SiC joint using anorthite based glass-ceramic and first principles calculation of joint interface

Joining SiC ceramics with ZrSi2–SiC filler at low temperatures

Joining silicon nitride ceramics with ZrSi2-SiC composite filler by spark plasma sintering

Low-temperature sintering of silicon carbide with Li2O-Al2O3-SiO2 melts as sintering aids

Joining of SiC Ceramic by Using the Liquid Polyvinylphenylsiloxane

Near-seamless joining of Cf/SiC composites using Y3Si2C2 via electric field-assisted sintering technique