Li-Xiang Wu,Lin-Lin Zhu,Wei-Ming Guo,Shi-Kuan Sun,Wen-Bin Niu,Jia-Xiang Xue,Jian-Han Zhai,Hai-Bin Ma,Rui-Lin Lin,Hua-Tay Lin,Kevin Plucknett,Ye-Hong Liao,Tong Liu,Qi-Sen Ren
Abstract:<p>The joining of liquid-phase sintered SiC (LPS-SiC) ceramics was conducted using spark plasma sintering (SPS), through solid state diffusion bonding, with Ti-metal foil as a joining interlayer. Samples were joined at 1400 °C, under applied pressures of either 10 or 30 MPa, and with different atmospheres (argon, Ar, vs. vacuum). It was demonstrated that the shear strength of the joints increased with an increase in the applied joining pressure. The joining atmosphere also affected on both the microstructure and shear strength of the SiC joints. The composition and microstructure of the interlayer were examined to understand the mechanism. As a result, a SiC-SiC joining with a good mechanical performance could be achieved under an Ar environment, which in turn could provide a cost-effective approach and greatly widen the applications of SiC ceramic components with complex shape.</p>
What problem does this paper attempt to address?
The paper primarily explores the effectiveness of using titanium foil as an interlayer to join liquid phase sintered silicon carbide (LPS-SiC) ceramic joints through solid-state diffusion bonding technology under different atmospheres (argon and vacuum) and different pressure conditions (10 MPa and 30 MPa). The core issue of the study is to find the optimal bonding conditions to improve the shear strength of the joints and to understand the impact of different processing conditions on the microstructure of the bonding area.
Specifically, the paper addresses the following key issues:
1. **Shear Strength Improvement**: The study found that as the bonding pressure increases, the shear strength of the joints also increases. In a vacuum environment, when the pressure increased from 10 MPa to 30 MPa, the shear strength reached 43.0±6.2 MPa and 91.9±3.0 MPa, respectively; whereas in an argon environment, the same pressure change resulted in shear strengths of 67.7±7.5 MPa and 109.3±4.5 MPa, respectively. This indicates that higher pressure helps to reduce the thickness of the interlayer, thereby reducing residual stress and improving shear strength.
2. **Effect of Bonding Atmosphere**: The paper points out that the bonding atmosphere also significantly affects the microstructure and shear strength of the joints. In a vacuum environment, the interlayer mainly consists of Ti5Si3, TiC, SiC, and a small amount of YAG, while in an argon environment, there is more YAG and SiC, and less Ti5Si3, which has a high thermal expansion coefficient. The formation of YAG helps to further reduce the thermal stress between the matrix and the interlayer, thereby enhancing mechanical shear strength.
3. **Microstructure of the Interlayer**: The study also provides a detailed analysis of the microstructure of the interlayer under different conditions. For example, in a vacuum environment, the interlayer exhibits a three-layer structure, with the central part mainly composed of TiC, while in an argon environment, the interlayer composition is more complex, including more YAG and SiC but less Ti5Si3. This structural change helps to reduce the thickness of the interlayer and the formation of Ti5Si3, thereby reducing residual stress and enhancing the reliability of the joints.
In summary, the paper aims to improve the performance of LPS-SiC ceramic joints, particularly their shear strength, by optimizing bonding parameters (such as pressure and atmosphere) and explores the impact of different processing conditions on the microstructure of the joints. These research findings are of great significance for expanding the application of complex-shaped SiC ceramic components.