Abstract:CaO-Al2O3-SiO2 system (CAS) glass-ceramics with anorthite crystal structure was prepared by melt-method. Its microstructure and morphology were characterized by differential thermal analysis (DTA), X-ray diffraction (XRD) and scanning electron microscope (SEM). The effects of TiO2 content on the relationship between microstructure and mechanical properties for the CAS glass-ceramics were also investigated by electron paramagnetic resonance (EPR) and the position annihilation technique (PAT). The results showed that the TiO2 content does not affect the type of the main crystalline phase of CAS glass-ceramics, but it could reduce the crystallization peak temperature and promote the crystallization. The relationship between g factor and bending strength showed that during the melting and heat-treatment process, part of the Ti4+ ions were reduced to Ti3+ and formed oxygen vacancies, the spin angular correlation between Ti3+-O-Ti3+ and oxygen vacancies affected the bending strength directly. The relationship between positron lifetime and bending strength showed that interval Ti4+ could make some defects and Al, Si vacancies, which could affect the mechanical properties. Electrostatic interaction between Ti4+ and O2- could make the independent oxonium ion into an integral, which was favourable to bending strength. When the TiO2 content was higher than 6%, some Si4+ were substituted by Ti4+, and the Ti-O bond was weaker than the Si-O bond, which led to a decrease in bending strength. When the content was 6%, the microhardness was 830 MPa, and the bending strength was 314 MPa in the heat treatment conditions of nucleation temperature 750°C, nucleation time 2 h, crystallization temperature 950°C, crystallization time 2 h.

Microstructure and mechanical properties of SiC joint using anorthite based glass-ceramic and first principles calculation of joint interface

Microstructure, Mechanical Property and Bonding Mechanism of SiC Ceramic Joint Using a Novel Y2Si2O7/Mullite Glass-Ceramic Interlayer

Joining of SiC ceramics using CaO-Al<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> (CAS) glass ceramics

Joining of SiC ceramics using CaO-Al2O3-SiO2 (CAS) glass ceramics

Microstructure Evolution and Mechanical Properties of Porous Si3N4 and Dense Si3N4 Joints Bonded Using CaO–Li2O-Al2O3–SiO2 Glass-Ceramic

Microstructure and Mechanical Property of Vacuum Brazed SiC Ceramic Joint

Joining of Cf/SiC composites and Si<sub>3</sub>N<sub>4</sub> ceramic with Y<sub>2</sub>O<sub>3</sub>-Al<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> glass filler for high-temperature applications

Microstructure and Shear Strength of SiC Joint Brazed with LiAlSiO4 Reinforced AgCuTi Composite Filler

Joining SiC ceramics with ZrSi2–SiC filler at low temperatures

Joining Dense Si3N4 to Porous Si3N4 Using a Novel Glass-Ceramic Interlayer with Precipitated Β-Lialsi2o6/mg2sio4

Effect of Brazing Parameters on the Microstructure and Properties of SiC Ceramic Joint with Zr-Cu Filler Metal

Microstructure and mechanical properties of SiC/SiC joints reinforced by in-situ growth SiC nanowires

Microstructure and Fracture Behavior of SiO 2 Glass Ceramic and TC4 Alloy Joint Brazed with TiZrNiCu Alloy

Effect of SiC Nanowires on the Thermal Shock Resistance of Joint Between Carbon/carbon Composites and Li2O–Al2O3–SiO2 Glass Ceramics

Microstructure and shear strength of SiC/Zr joint brazed with LiAlSiO4/graphene-coated Cu-foam composite interlayer

Study on the mechanism of glass-SiC-glass anodic bonding process

Microstructure and Formation Mechanism of Cf/SiC and Nb Joint Brazed with Laminated Amorphous Ti–Zr–Cu–Ni/crystalline Ti Composite Filler

SiC nanowires reinforced MAS joint of SiC coated carbon/carbon composites to LAS glass ceramics

Microstructure and mechanical properties of the CaO-Al2O3-SiO2 system glass-ceramics

Interface microstructure and mechanism of SiC ceramic vacuum brazed joint

Mechanical and electrical properties of reaction-formed joints in silicon carbide ceramic materials