Effect of Brazing Parameters on the Microstructure and Properties of SiC Ceramic Joint with Zr-Cu Filler Metal

Bofang Zhou,Jinfeng Wang,Keqin Feng,Yuchen Cai,Sitan Chen

DOI: https://doi.org/10.3390/cryst10020093

IF: 2.7

2020-02-06

Crystals

Abstract:The microstructure and mechanical properties of brazing SiC ceramic with Zr-Cu filler metal under different brazing parameters (brazing temperature, holding time) were investigated. The phase of the joint reaction interface between Zr-Cu filler metal and SiC ceramic was characterized by XRD, the microstructure and fracture morphology of the brazing SiC ceramic joint were analyzed by SEM with EDS, and the strength of the joint was evaluated by compression shear test. The results show that the brazing join between SiC ceramic and Zr-Cu filler metal can be realized at the brazing temperature of 1100 °C~1300 °C, and the main products of interface reaction are ZrC and Zr2Si. The shear strength of the joint increases with the brazing temperature, and reaches the highest at 1200 °C. The thickness of interface reaction layer increases with the increase of holding time at brazing temperature of 1200 °C. Thickness of the interface reaction layer is 2.9 μm when the joint is holding for 20 min, and the maximum shear strength of the corresponding brazed SiC ceramic joint is 57 MPa.

materials science, multidisciplinary,crystallography