Microstructure and mechanical properties of ZrB 2 ‐SiC/Nb joints brazed with CoFeNiCrCuTi x high‐entropy alloy filler

Yunlong Yang,Gang Wang,Rujie He,Da Shu,Caiwang Tan,Wei Cao
DOI: https://doi.org/10.1111/jace.17732
IF: 4.186
2021-03-04
Journal of the American Ceramic Society
Abstract:<p>ZrB<sub>2</sub>‐SiC ceramics and Nb alloy were brazed at 1160°C for 60 min with CoFeNiCrCuTi<sub>x</sub> high‐entropy alloy filler. The influence of Ti content on the interface structure and mechanical properties of ZrB<sub>2</sub>‐SiC/Nb joint was systematically studied. It is found that the rich‐Ti Laves phase was formed due to the addition of large atomic size Ti fill into the filler alloy or brazing joint, and its content increases with Ti content. The joint brazed by high‐entropy alloys filler without Ti can be divided into a tooth‐shaped Cr<sub>2</sub>B reaction layer and a central area composed of a eutectic mixed structure of FCC phase and rich‐Nb lamellar Laves phase. Ti and Nb are mutual solid solution elements. The increase of Ti content in the joint makes the FCC phase and the rich‐Nb lamellar Laves phase to transform into a big bulk Ti‐rich Laves phase and the quadrilateral (Ti, Nb)B phase. The tooth‐shaped Cr<sub>2</sub>B was disappeared. The residual stress generated in the joint during the brazing process tends to cause defects such as holes and microcracks in the bulk Ti‐rich brittle Laves phase. Therefore, with the addition of Ti, the normal temperature performance of the joint decreases from 216 MPa to 52 MPa. However, with the increase of Ti, the high‐temperature mechanical properties of the joint first decrease, and then increase. It was mainly due to the formation of rich‐Ti Laves phase and quadrilateral (Ti, Nb)B with excellent high‐temperature mechanical properties. When brazing with CoFeNiCrCuTi<sub>1.5</sub> filler, the high temperature performance of the joint reached 92% of its room temperature performance.</p>
materials science, ceramics
What problem does this paper attempt to address?
The problem that this paper attempts to solve is: how to improve the connection performance between ZrB2 - SiC ceramics and Nb alloy by adding different contents of titanium (Ti) to high - entropy alloy (CoFeNiCrCuTix) filler metals. Specifically, the research aims to explore the influence of Ti content on the microstructure and mechanical properties of ZrB2 - SiC/Nb joints, especially on the shear strength of the joints at room temperature and high temperature. ### Research Background 1. **Material Characteristics** - Ceramic materials (such as ZrB2 - SiC) have excellent physical, chemical and high - temperature properties and are widely used in the aerospace field. - The combination of metals (such as Nb alloy) and ceramics can take advantage of both, but there are some fundamental problems: - Metals are difficult to wet ceramics because there is a mismatch in the bonding type between metals and ceramics. - The difference in the coefficient of thermal expansion (CTE) between metals and ceramics is large, and residual stress and even cracks are easily generated at the interface. 2. **Existing Technologies** - Brazing is an efficient, high - quality, simple and effective method for connecting ceramics and metals. - Although traditional active filler materials (such as Ni - Ti) have good high - temperature properties, a large amount of brittle intermetallic compounds are easily generated during the brazing process, resulting in a decline in joint performance. ### Research Objectives - **Optimize Brazing Process**: By adding different contents of titanium (Ti) to high - entropy alloy (CoFeNiCrCu), study its influence on the microstructure and mechanical properties of ZrB2 - SiC/Nb joints. - **Improve Joint Performance**: In particular, improve the shear strength of the joints at room temperature and high temperature, and reduce the generation of defects (such as pores and micro - cracks). ### Main Research Contents 1. **Experimental Design** - Use CoFeNiCrCuTix high - entropy alloys with different Ti contents (x = 0, 0.5, 1.5) as filler metals. - Conduct brazing experiments at 1160°C for 60 minutes. 2. **Result Analysis** - **Microstructure**: Analyze the microstructure of the joints by scanning electron microscope (SEM), energy - dispersive X - ray spectroscopy (EDS) and X - ray diffraction (XRD). - **Mechanical Properties**: Measure the shear strength of the joints at room temperature and 650°C. 3. **Conclusion** - After adding Ti, the room - temperature shear strength of the joints decreases significantly, from 216 MPa to 52 MPa (x = 1.5). - The high - temperature (650°C) shear strength first decreases and then increases. Especially when the Ti content is 16.7 at.%, the high - temperature shear strength is close to 92% of the room - temperature shear strength. - This is mainly due to the formation of Ti - rich Laves phase and tetragonal (Ti, Nb)B phase, which have excellent high - temperature mechanical properties. ### Solution By adding an appropriate amount of Ti to the high - entropy alloy filler metal, the high - temperature mechanical properties of ZrB2 - SiC/Nb joints can be significantly improved, although the room - temperature performance decreases. This finding provides new ideas and technical means for the development of high - performance ceramic - metal joints.