Abstract:MgO-Al2O3-SiO2 (MAS) glass-ceramics were prepared by traditional melting and sintering method, and the effects of MgO/Al2O3 ratios and La2O3 contents on the microstructure and physicochemical properties of MAS glass-ceramics were studied. Herein, differential scanning calorimetry (DSC), X-ray diffraction (XRD), fourier-transform infrared spectrophotometer (FTIR), Field-emission scanning electron microscopy (FESEM), density, corrosion resistance, dielectric properties and thermal expansion coefficient (CTE) were carried out to evaluate the properties of both parent glass and glass-ceramics samples. The results show that adjusting the MgO/Al2O3 ratio from 0.69 to 0.47 can increase the characteristic temperatures of transition temperature (T g ) and crystallization peak temperature (T p ) in MAS parent glass. The reduction of MgO/Al2O3 ratio could promotes the precipitation of α-cordierite phase (Mg2Al4Si5O18), and the grain size of α-cordierite phase were increased from 200 to 500 nm. When the MgO/Al2O3 ratio was 0.63, the MA-2 sample has the highest flexural strength of 127.46 MPa. Furthermore, we also investigated the influence of La2O3 addition on the structure and properties of MAS glass-ceramics by employed MA-2 sample as a reference. The results show both the T g (742–748 °C) and T p (936–943 °C) of parent glass exhibit a slightly increasing with the La2O3 content was increased from 0.0 to 2.0 wt%. The La2O3 addition show a negligible influence on the crystal phase and morphology of MAS glass-ceramics. With increasing of the La2O3 content, the MAS glass-ceramics samples have a larger density (2.58–2.76 g/cm3) and a better chemical stability, and the CTE (6.12–8.17 × 10−6/°C), ε r (5.04–6.17), and the flexural strength (127.46–150.15 MPa) also show an increased change trends. The prepared MAS glass-ceramics can be packaged with high expansion coefficient chips (such as GaAs) and is expected to become a potential candidate of dielectric materials for electronic devices, especially for high frequency applications in integrated circuits.

Microstructure, mechanical and optical properties of MgAl2O4/MgAl2O4 joints bonded using CaO-Al2O3-SiO2 glass filler

Interfacial evolution mechanism of MgAl2O4/MgAl2O4 joints bonded with lanthanum glass

Joining MgAl2O4 ceramics using ZnO–Al2O3–SiO2 glass ceramic with precipitated ZnAl2O4

Joining of SiC ceramics using CaO-Al2O3-SiO2 (CAS) glass ceramics

Research on the interfacial microstructure and mechanical properties of glass/Mg joint prepared by anodic bonding and vacuum diffusion bonding

Microstructure and Properties of Porous Si3N4/Dense Si3N4 Joints Bonded Using RE–Si–Al–O–N (RE = Y or Yb) Glasses

Novel design of sapphire/spinel transparent ceramic joints with double glass interlayers by coating and bonding

Microstructure and Properties of Porous Si3N4/Dense Si3N4 Joints Bonded Using RE-Si-Al-O-N (RE = Y or Yb) Glasses

High-performance flash joining of MgAl2O4 transparent ceramics

Joining transparent spinel ceramics using refractive index–matched glass

Mixed CaO/MgO effect on microstructure, mechanical properties and crystallization behaviour of Li2O-Al2O3-SiO2-ZrO2-P2O5 glass

Alumina joints brazed by screen-printed B4C–SiO2 in air

Effects of MgO/CaO ratio on the crystal phase composition and performance of MgO-CaO-B2O3-SiO2 glass–ceramics for LTCC applications

Microstructure and mechanical properties of SiC joint using anorthite based glass-ceramic and first principles calculation of joint interface

Microstructure and mechanical properties of the CaO-Al2O3-SiO2 system glass-ceramics

Preparation and characterization of MgO-Al2O3-SiO2 glass-ceramics with different MgO/Al2O3 ratio and La2O3 addition

Joining high volume fraction SiC particle reinforced aluminum matrix composites using Bi2O3-B2O3-ZnO-BaO-Na2O glass

Pressure-less joining of SiCf/SiC composites by Y2O3–Al2O3–SiO2 glass: Microstructure and properties

Joining AlN ceramics by ZnO–Al2O3–B2O3–SiO2 (ZABS) glass-ceramic at low temperature

Effect of SiO2/Al2O3 ratio on the structure and electrical properties of MgO–Al2O3–SiO2 glass-ceramics doped with TiO2

Influence of CaO on microstructure and properties of MgAl2O4 transparent ceramics