Abstract:MgO-Al2O3-SiO2 (MAS) glass-ceramics were prepared by traditional melting and sintering method, and the effects of MgO/Al2O3 ratios and La2O3 contents on the microstructure and physicochemical properties of MAS glass-ceramics were studied. Herein, differential scanning calorimetry (DSC), X-ray diffraction (XRD), fourier-transform infrared spectrophotometer (FTIR), Field-emission scanning electron microscopy (FESEM), density, corrosion resistance, dielectric properties and thermal expansion coefficient (CTE) were carried out to evaluate the properties of both parent glass and glass-ceramics samples. The results show that adjusting the MgO/Al2O3 ratio from 0.69 to 0.47 can increase the characteristic temperatures of transition temperature (T g ) and crystallization peak temperature (T p ) in MAS parent glass. The reduction of MgO/Al2O3 ratio could promotes the precipitation of α-cordierite phase (Mg2Al4Si5O18), and the grain size of α-cordierite phase were increased from 200 to 500 nm. When the MgO/Al2O3 ratio was 0.63, the MA-2 sample has the highest flexural strength of 127.46 MPa. Furthermore, we also investigated the influence of La2O3 addition on the structure and properties of MAS glass-ceramics by employed MA-2 sample as a reference. The results show both the T g (742–748 °C) and T p (936–943 °C) of parent glass exhibit a slightly increasing with the La2O3 content was increased from 0.0 to 2.0 wt%. The La2O3 addition show a negligible influence on the crystal phase and morphology of MAS glass-ceramics. With increasing of the La2O3 content, the MAS glass-ceramics samples have a larger density (2.58–2.76 g/cm3) and a better chemical stability, and the CTE (6.12–8.17 × 10−6/°C), ε r (5.04–6.17), and the flexural strength (127.46–150.15 MPa) also show an increased change trends. The prepared MAS glass-ceramics can be packaged with high expansion coefficient chips (such as GaAs) and is expected to become a potential candidate of dielectric materials for electronic devices, especially for high frequency applications in integrated circuits.

Joining MgAl2O4 ceramics using ZnO–Al2O3–SiO2 glass ceramic with precipitated ZnAl2O4

Microstructure, mechanical and optical properties of MgAl2O4/MgAl2O4 joints bonded using CaO-Al2O3-SiO2 glass filler

Joining AlN ceramics by ZnO–Al2O3–B2O3–SiO2 (ZABS) glass-ceramic at low temperature

Interfacial evolution mechanism of MgAl2O4/MgAl2O4 joints bonded with lanthanum glass

Joining high volume fraction SiC particle reinforced aluminum matrix composites using Bi2O3-B2O3-ZnO-BaO-Na2O glass

Microstructure and Properties of Porous Si3N4/Dense Si3N4 Joints Bonded Using RE–Si–Al–O–N (RE = Y or Yb) Glasses

Pressure-less joining of SiCf/SiC composites by Y2O3–Al2O3–SiO2 glass: Microstructure and properties

Microstructure and Properties of Porous Si3N4/Dense Si3N4 Joints Bonded Using RE-Si-Al-O-N (RE = Y or Yb) Glasses

Joining of SiC ceramics using CaO-Al2O3-SiO2 (CAS) glass ceramics

Enhanced bonding strength of Al2O3/AlN ceramics joined via glass frit with gradient thermal expansion coefficient

Microstructure evolution and mechanical properties of YAG/YAG joint using bismuth-borate glass

Microstructure and Mechanical Properties of Al2O3/Cu Joints Brazed with Ag–Cu–Ti+Zn Composite Fillers

Preparation and characterization of MgO-Al2O3-SiO2 glass-ceramics with different MgO/Al2O3 ratio and La2O3 addition

Impact of ZnO content in BAS glass–ceramics and pre‐oxidation temperature on Kovar alloys to their sealing strength

Microstructure and formation mechanism of Al2O3/Zn5Al/2024Al joint by ultrasonic assisted soldering process

Realizing the air brazing of ZrO2 ceramics through Al metal

Mixed CaO/MgO effect on microstructure, mechanical properties and crystallization behaviour of Li2O-Al2O3-SiO2-ZrO2-P2O5 glass

Joining Mg Alloys with Zn Interlayer by Novel Ultrasonic-Assisted Transient Liquid Phase Bonding Method in Air

Microstructure and shear strength of SiC/Zr joint brazed with LiAlSiO4/graphene-coated Cu-foam composite interlayer

Crystallization Behavior and Performance of MgO-Al2O3-SiO2 Glass-Ceramics by Sintering

PHASE TRANSITION AND PROPERTIES OF Li_2O - Al_2O_3 - SiO_2 SYSTEM GLASS- CERAMIC WITH PARTIAL REPLACEMENT OF Al_2O_3 BY ZnO