Microstructure evolution and mechanical properties of YAG/YAG joint using bismuth-borate glass

Jincheng Lin,Panpan Lin,Run Ao,Lili Xing,Tiesong Lin,Peng He,Jian Li,Weiqi Yang

DOI: https://doi.org/10.1016/j.jeurceramsoc.2020.12.002

IF: 5.7

2021-04-01

Journal of the European Ceramic Society

Abstract:<p>Joining of Y₃Al₅O₁₂ garnet single crystal (YAG) was achieved by using a bismuth-borate based glass filler. The thermal properties of glass filler were experimentally determined and the wettability of molten glass on YAG was investigated. The YAG reacted with glass to form ZnAl₂O₄ particles and Y₂O₃ nanowires successively as joining temperature is above 625℃. ZnAl₂O₄ preferentially nucleated and grew on Y₂O₃ nanowires. The cooperative growth of the two phases accelerated YAG decomposition, which in turn led to cluster growth of Y₂O₃ nanowires and aggregation of ZnAl₂O₄ particles at elevated temperature. The microstructure evolution and reaction mechanism were studied. The highest shear strength of 29.6 ± 5.2 MPa was obtained for the joint brazed at 650℃. The fracture morphology demonstrated that the dispersive strengthening of ZnAl₂O₄ and stress relief by Y₂O₃ nanowire network contributed to the superior mechanical performance.</p>

materials science, ceramics