Abstract:In order to improve the strength of Cu/Al2 O3 joint, vacuum brazing of copper to Al2 O3 ceramic was performed using nano -Al2O3 strengthened AgCuTi composite filler ( abbreviated as AgCuTip filler ). The microstructure and mechanical performance of the brazed joint were investigated by scanning electron microscope ( SEM ) , energy dispersive spectrometer ( EDS ) and shear strength test. Typical interfacial microstructure of Cu/AgCuTip/Al2O3 brazed joint is Cu/diffusion layer/Cu-based solid solution + Ag-based solid solution+Ti2 Cu +Ti3( Cu, Al) 3 O/Al2 O3 . The addition of nano-Al2 O3 can improve the interfacial microstructure by inhibiting the growth of reaction layer near Al2 O3 ceramic side, and promoting the formation of dispersed Ti2 Cu phase in brazing seam. Moreover, both thickness of diffusion layer and Ti3(Cu, Al)3O reaction layer thickened with an increasing holding time. Excessive dissolution of copper was occurred when holding time reached 20 min, which deteriorated the performance of the brazed joint. The highest shear strength of 82 MPa can be obtained when brazed at 880 °C for 10 min. The addition of nano-Al2O3 particles can refine the microstructure of brazing seam and decrease the mismatch of coefficient of thermal expansion between substrates and brazing seam. Therefore, the performance of brazed joint can be improved. The holding time can affect the microstructure and thickness of reaction layer, thereby affect the strength of brazed joints.

Active brazing of YAG crystal and Cu using AgCuInTi filler: Microstructure and joint properties

Wettability and microstructure transformations of YAG ceramic brazing to kovar alloy with AgCuTi filler alloy

Microstructure and properties of a YG18/40Cr joint vacuum–brazed by Cu–Sn–Ti filler metal

Microstructure evolution and mechanical properties of YAG/YAG joint using bismuth-borate glass

Microstructures and mechanical properties of YG18 cemented carbide/40Cr steel joints vacuum brazed using Ag–Cu–Ti filler metal

Wetting and Brazing of YIG Ceramics Using Ag–CuO–TiO2 Metal Filler

Reactive air brazing of YSZ ceramic with novel Al2O3 nanoparticles reinforced Ag-CuO-Al2O3 composite filler: Microstructure and joint properties

Brazing YSZ ceramics by a novel SiO2 nanoparticles modified Ag filler

Microstructure and mechanical properties of Al2O3 ceramic and copper joints brazed with AgCuInTi brazing alloy

Microstructural Evolution of Si3n4/Ti6al4v Joints Brazed with Nano-Si3n4 Reinforced Agcuti Composite Filler

Microstructure and mechanical properties of Si3N4 ceramic and (TiB + Y2O3)/Ti matrix composite joints brazed with AgCu/Cu foam/AgCu multilayered filler

Microstructure and Performance of the Cu/Al2O3 Joint Brazed with Active Composite Filler

Interfacial Microstructure and Mechanical Property of SiO2-BN Ceramics and Invar Joint Brazed with Ag–Cu–Ti Active Filler Metal

Microstructure and Mechanical Properties of Al2O3/Cu Joints Brazed with Ag–Cu–Ti+Zn Composite Fillers

Interfacial microstructure and mechanical property of ZrC-SiC ceramic and TiAl joint brazed with AgZr active filler metal

Microstructure and mechanical properties of single-crystal diamond/Kovar alloy joints brazed with an AgCuTi metal filler

Interfacial Microstructure and Mechanical Property of Brazed Copper/sio2 Ceramic Joint

Microstructure evolution and mechanical properties of ZrO 2 /TiAl joints vacuum brazed by Ag–Cu filler metal

Microstructure and Mechanical Properties of Invar Alloy and Si3N4 Ceramic Brazed Joints

Brazing of micrograin-filled quartz fiber reinforced silica composites and Invar using Ag-21Cu-4.5Ti alloy

Interfacial microstructure and mechanical properties of porous-Si3N4 ceramic and TiAl alloy joints vacuum brazed with AgCu filler