Abstract:The brazed joint of sapphire transparent ceramic and Kovar alloy was prepared using AgCuTi and AgCuTiB composite filler, and the main focus was the effect of B element on the wetting behavior, interface composition and joint mechanical performance. The reliable joint of sapphire transparent ceramic and Kovar alloy was obtained by vacuum brazing with AgCu28-6Ti-0.45B (wt%) composite filler. The typical interfacial structure of the joint brazed at 825 °C for 10 min was determined as sapphire/Ti 3 Cu 3 O/Ag(s,s) + Cu(s,s) + disperse TiB/TiFe 2 + TiNi 3 /Kovar. The results showed that the addition of B could contributed to an optimized interfacial structure via (i) in-situ forming fine TiB whisker reinforcement phase and refining the interface structure and (ii) reducing the diffusion degree of alloy side elements to inhibit the generation of brittle phase, and the maximum shear strength of the joint with AgCu28-6Ti-0.45B (wt%) reached 125 MPa more than twice the joint without B additive. On the other hand, the wetting experiment showed that the addition of B as a solid particle decreased the fluidity of the composite filler, and when the addition of B was excessive, no dense TiB whiskers were produced in the interface. This study provides ideas for the optimization and improvement of sapphire composite connection, and points out that the generation of reinforcing phase is accompanied by the reduction of fluidity, so it is necessary to reasonably control the proportion of reinforcing phase.

Microstructure and mechanical properties of single-crystal diamond/Kovar alloy joints brazed with an AgCuTi metal filler

Brazing of diamond to invar with Ag-Cu-Ti filler alloy: Wettability, microstructure and mechanical performance

Improvement of microstructure and mechanical properties of Sapphire/Kovar alloy joints brazed with Ag-Cu-Ti composite filler by adding B powders

A novel CoCrNi medium entropy alloy enhanced AgCuTi composite filler to braze Kovar alloy and sapphire

Interfacial Structure of Diamond Brazing with Cu-Sn-Cr

Microstructure and Mechanical Properties of Al2O3/Cu Joints Brazed with Ag–Cu–Ti+Zn Composite Fillers

Microstructure and mechanical properties of Al2O3 ceramic and copper joints brazed with AgCuInTi brazing alloy

Effect of Cu interlayer with different thickness on microstructure and properties of Al2O3/Kovar joints brazed with Cu–Ti/Cu/BNi-2 composite filler

Microstructure and Mechanical Properties of Pre-Brazed Diamond Abrasive Grains Using Cu–Sn–Ti Alloy

A new low-temperature preparation technology of heat-resistant diamond/Cu joint using composite braze: microstructure evolution and mechanical properties strengthening

Wettability and microstructure transformations of YAG ceramic brazing to kovar alloy with AgCuTi filler alloy

Microstructure and mechanical properties of TC4 joints brazed with Ti–Zr–Cu–Sn amorphous filler alloy

Microstructure and properties of the TiAl/GH3030 dissimilar joints vacuum-brazed with a Ti-based amorphous filler metal

A high-strength vacuum brazed TC4/316L joint with a Ti–Zr-based amorphous ribbon as the filler metal

Microstructure and mechanical properties of Si3N4 ceramic and (TiB + Y2O3)/Ti matrix composite joints brazed with AgCu/Cu foam/AgCu multilayered filler

Microstructure and properties at bonds of diamond grains and Ni Cr filler alloy by fiber laser brazing

Microstructural evolution and mechanical property of a SiCf/SiC composite/Ni-based superalloy joint brazed with an Au-Cu-Ti filler

Interfacial microstructure and mechanical properties of WC–Co/40Cr joints brazed at low–temperature with Ag–Cu–Ti + Sn novel filler

Effect of Interface Microstructure on Joint Strength of Zirconia/Titanium Alloy Brazed with Amorphous Zr-Ti-Ni-Cu Active Filler Metal

Active brazing of YAG crystal and Cu using AgCuInTi filler: Microstructure and joint properties

Microstructure evolution and mechanical properties of TiAl/GH536 joints vacuum brazed with Ti–Zr–Cu–Ni filler metal