PHASE TRANSITION AND PROPERTIES OF Li_2O - Al_2O_3 - SiO_2 SYSTEM GLASS- CERAMIC WITH PARTIAL REPLACEMENT OF Al_2O_3 BY ZnO

HUAnmin,LI Ming,MAO Dali,LIANG Kaiming

DOI: https://doi.org/10.3321/j.issn:0454-5648.2005.08.016

2005-01-01

Abstract:The effect of replacement of 0-15% (in mass fraction, the same below) Al2O3 by ZnO on the crystallization behaviors and properties of Li2O- Al2O3-SiO2 glass-ceramic was investigated. The results show that with increasing ZnO content, the melting temperature of glass, the glass transition temperature and crystallization temperature were lowered. All glass-ceramics with different compositions can have fine equiaxial crystalline microstructures and low thermal expansion coefficient. With the replacement of 5% , β- quartz solid solution precipitated first, then β- spodumene with increasing temperatures. No changes were observed in structure or properties; they remained almost the same as the samples without replacement. When the replacement was increased to 10% with crystallization at 820℃ , willemite appeared in addition to β- quartz solid solution and β- spodumene. Then the samples had higher flexural strength and fracture toughness. When the replacement was increased to 15%, crystals tended to become coarser, which could result in a decrease in the flexural strength and fracture toughness.