Abstract:The improvement of glass and glass ceramics mechanical performance, which is determined by the components and structures, has become a critical issue for various applications. In current research, alkaline earth oxides, MgO and CaO, were introduced into Li2O-Al2O3-SiO2 glass components for glass better mechanical properties. The dependency of CaO/MgO ratios on the glass structures were investigated by Raman and nuclear magnetic resonance spectroscopy. The conversion of Qn groups in glass network confirmed decreasing bridging oxygen and connectivity with the increased CaO/MgO ratios. The glass densities, molar volumes showed linear increase with the replacement small Mg2+ion with large Ca2+ ion in glass structures. The glass transition and first crystallization temperatures slightly dropped with higher CaO content, until MgO was completely replaced. The non-linear glass hardness with maximum deviation from end numbers indicated the mixed alkaline effect in Li2O-Al2O3-SiO2 glass, probably originated from the chemical bonds and topological constraints due to the coexistence of Mg and Ca in glass structure. After heat-treatment, MgAl2Si4O12 and SiO2 crystals were precipitated in Li2O-MgO-Al2O3-SiO2 glass matrix, and the crystals phases changed to the combination of MgAl2Si4O12, LiAlSi3O8, and SiO2, to LiAlSi3O8, SiO2, to LiAlSi3O8, SiO2, ZrSiO4, and finally to Li2O·Al2O3·7.5SiO2, SiO2, ZrSiO4, due to the changed ion radius and contents, with the increased CaO/(MgO+CaO) ratios. Meanwhile, the diameters of crystals grew larger. The hardness and Reduced elastic modulus of glass ceramics increased at first, from 8.30 to maximum 8.67 GPa, and from 74.00 to 84.20 GPa, with 0.2 CaO/(MgO+CaO) ratio and then dropped. The glass structures, crystals phases and sizes change were responsible for the different mechanical properties.

The Role of Phosphate in the Glass Forming Region, Structure and Mechanical Properties for the SiO2-Al2O3-P2O5 System Contains High-Aluminum

Ab Initio Molecular Dynamics Simulation of Structural and Elastic Properties of SiO2–P2O5–Al2O3–Na2O Glass

Mechanical–Structural Investigation of Chemical Strengthening Aluminosilicate Glass Through Introducing Phosphorus Pentoxide

A Novel Method for Preparing Phase-Separated P2O5–Al2O3 Glass with High Young's Modulus

The structure and properties of chemical strengthened transparent lithium disilicate glass ceramics with various P2O5 contents

Phosphate/Silicate Ratio Allows for Fine-Tuning of Bioactive Glass Crystallisation and Glass-Ceramic Microstructure

A Modified Random Network Model for P2O5–Na2O–Al2O3–SiO2 Glass Studied by Molecular Dynamics Simulations

Mixed CaO/MgO effect on microstructure, mechanical properties and crystallization behaviour of Li2O-Al2O3-SiO2-ZrO2-P2O5 glass

Investigation of the P2O5–Bi2O3–CaO system: Glass forming region, structure, properties

Effects of SiO2 on Properties and Structures of Neodymium Doped P2O5-Al2O3-Li2O-MgO-Sb2O3 Glasses

Effect of Recombination Time on the Structure and Properties of P2O5-Al2O3 Heterogeneous Composite Glass

Dispersion, ionic bonding and vibrational shifts in phospho-aluminosilicate glasses

Insights into the Iron- and Phosphorus-Induced Structural Rearrangements in Sodium Aluminoborosilicate Glasses and Their Impact on Melt Rheology and Crystallization Behavior

Effects of Phosphorus Pentoxide Content on Ion Exchange Performance of Aluminosilicate Glasses

Glass Formation and Structure of Calcium Antimony Phosphate Glasses and Those Doped with Tellurium Oxide

FTIR, Raman and NMR Investigation of CaO–SiO2–P2O5 and CaO–SiO2–TiO2–P2O5 Glasses

La2O3 Substitution in Li-Al-P-O-N Glasses for Potential Solid Electrolytes Applications

Effect of Al<sub>2</sub>O<sub>3</sub> on Sound Velocity of MgSiO<sub>3</sub> Glass at High Pressure

Effect of Al_2O_3 on structure and properties of Al_2O_3-K_2O-P_2O_5 glasses

PHASE TRANSITION AND PROPERTIES OF Li_2O - Al_2O_3 - SiO_2 SYSTEM GLASS- CERAMIC WITH PARTIAL REPLACEMENT OF Al_2O_3 BY ZnO

FTIR and XPS studies of low-melting PbO-ZnO-P2O2 glasses