Effects of Li2O replacing Na2O on glass forming, structure and properties of Na2O–MgO–Al2O3–SiO2 glass and glass-ceramics

Yao He,Xuefeng Shen,Yong Jiang,Anxian Lu

DOI: https://doi.org/10.1016/j.matchemphys.2020.123865

IF: 4.778

2021-01-01

Materials Chemistry and Physics

Abstract:Glasses and glass-ceramics in the xLi2O-(5-x)Na2O–20MgO–20Al2O3–54SiO2 system have been prepared by using a conventional melt quenching technology and subsequently a two-step heat-treating method. The effects of Li2O replacing Na2O on crystallization, structural and electrochemical properties of Na2O–MgO–Al2O3–SiO2 glasses and glass-ceramics are studied. The results reveal that the glass forming ability, the bending strength, micro-hardness and ionic conductivity of parent glasses firstly decrease and then increase as Li2O gradually replacing Na2O from 0 mol.% to 5 mol.% due to the disconnection of Si–O–Si network, the suppression of the mobile species and the electrodynamic interaction between the Na–O- and Li–O- oscillating electric dipoles. The main crystalline phase of glass-ceramics is cordierite and the ionic conductivity is three orders of magnitude higher than that glasses. The ionic conductivity of MgO–Al2O3–SiO2 glass-ceramics with 5.0 mol.% Li2O replacing Na2O reaches the highest ionic conductivity (3.4 × 10−6 S/cm), which provides a potential application for glass-ceramics as solid electrolytes in the future.

materials science, multidisciplinary