Effect of Na+ Ions on the Mechanical Properties of Lithium Aluminosilicate Glass

Yanhang Wang,Lei Liu,Min Liu,Xianzi Li,Zhenyuan Zhang,Jiayu Liu,Xianying Shao,Yuebo Hu

DOI: https://doi.org/10.1134/s108765962360076x

2024-03-10

Glass Physics and Chemistry

Abstract:A series of lithium aluminosilicate glasses with the composition of 70SiO 2 –10Al 2 O 3 –5K 2 O–15Li 2 O– x NaCl ( x = 0.5, 1.5, 2.5, 3.5 and 4.5 wt %) were prepared by the melt-quenching method. The effect of NaCl addition on mechanical properties was assessed. It was found that both the glass density and the hardness decreased with increasing content of NaCl from 0.5 to 3.5 wt %. Interestingly, Vickers hardness of the glass increased when NaCl content increased by 4.5 wt %. Raman test results show that NBO/T in the glass increases with NaCl, that is, the decrease of the degree of polymerization of the glass network due to the breaking of Si–O–Si bonds. Since the Si–O–Si covalent bond is the strongest bond in the silicate glass, the glass structure tends to be depolymerized, and the density and Vickers hardness decrease. Thus, we attribute the hardness increasing at 4.5 wt % NaCl addition to the fact that Na + enters the network pores acting as network modifier.

materials science, ceramics