Crystallization Mechanism and Microstructure Evolution of Li 2 O–Al 2 O 3 –sio 2 Glass-Ceramics with Ta 2 O 5 As Nucleating Agent
Yaohui Li,Kaiming Liang,Bo Xu,JianWei Cao
DOI: https://doi.org/10.1007/s10973-009-0598-y
IF: 4.755
2009-01-01
Journal of Thermal Analysis and Calorimetry
Abstract:Li 2 O–Al 2 O 3 –SiO 2 glass-ceramics were prepared with Ta 2 O 5 as nucleating agent, the crystallization mechanism and microstructure evolution were investigated by DTA, XRD, and SEM technologies. With increasing amount of Ta 2 O 5 from 2 to 6 mol%, the crystallization activation energy decreased from 297.73 to 218.66 kJ mol −1 , while the crystallization index increased from 1.76 to 3.39. In addition, the cluster of dendritic crystals and lamellar structure obtained in T-2 glass-ceramics indicated a typical two-dimensional crystallization mechanism, and the formation of spherical β-quartz solid solution in T-4 specimens, with average size of 50–70 nm, was mainly due to bulk crystallization mechanism. It was considered that Ta 2 O 5 promoted the nucleation and crystallization of LAS glass by precipitating the crystalline precursor phase of Ta 2 O 5 , which acted as nuclei for the subsequent crystal growth. Eventually, the diffusion and crystallization process, microstructure morphology, as well as the secondary grain growth were also investigated.