Effect of Nucleation Temperatures and Time on Crystallization Behavior and Properties of Li2O–Al2O3–SiO2 Glasses

An-Min Hu,Kai-Ming Liang,Ming Li,Da-Li Mao

DOI: https://doi.org/10.1016/j.matchemphys.2005.09.060

IF: 4.778

2006-01-01

Materials Chemistry and Physics

Abstract:The crystallization behavior of Li2O–Al2O3–SiO2 glasses samples nucleated at different temperature and time (745°C/2h, 745°C/6h and 760°C/6h) was investigated by DTA, XRD and SEM. After nucleated at 745°C for 2 and 6h, the Avrami constants for the glass samples were 3.5–3.6 and activation energies of crystal growth were 276±3 and 280±5kJmol−1. The Avrami constant was 2.8 and activation energy of crystal growth was 302±6kJmol−1 for samples nucleated at 760°C for 6h. The crystallized phase was identified as h-quartz solid solution and SEM observations indicated that glass–ceramic samples have fine grained microstructure which indicates bulk crystallization. With increasing nucleation temperature to 760°C, the grain size increased and the values of flexural strength, hardness and fracture toughness decreased.