Effect of CeO2 on Microwave Dielectric Properties of MgO–Al2O3–SiO2–TiO2 Glass-Ceramic
Jiangang Wang,Wei Chen,Lan Luo
DOI: https://doi.org/10.1143/jjap.46.5218
IF: 1.5
2007-01-01
Japanese Journal of Applied Physics
Abstract:Glass-ceramics with a molar composition of 1.0MgO center dot 1.2Al(2)O(3)center dot 2.8SiO(2)center dot 1.2TiO(2)center dot xCeO(2), x = 0.2, 0.4, 0.6, and 0.8, were prepared by one-step crystallization heat treatment of the parent glasses at 1150 degrees C for 2h. The effects of CeO2 on crystalline phases, microstructure and microwave dielectric properties of the materials were investigated. The investigation shows that the glass-ceramics consist of three main crystalline phases. With the increase in CeO2, the perrierite phase (Ce2Ti2Si2O11) increases, while the rutile (TiO2) and alpha-cordierite (Mg2Al4Si5O18) phases decrease. At the same time, the quality factor (Q x f, Q = 1 / tan 6, f = resonant frequency) of the material increases slightly from 12,500 to 15,300 GHz, but the temperature coefficient of resonant frequency (tau(f)) of the material decreases markedly from + 116 to -5 ppm/degrees C because of the decrease in the rutile phase. The dielectric constant (8,) of the material is in the range of 10.4-12.6, and it increases first when CeO2 increases and then decreases, with the maximum value appearing at x = 0.6. Glass-ceramic with excellent microwave dielectric properties of epsilon(r) = 10.4, Q x f = 15,300 GHz, tau(f) = -5 ppm/degrees C, was obtained in this study.