Crystallization kinetics, structural and mechanical properties of transparent lithium aluminosilicate glass-ceramics
Xinyue Zhang,Jing Wang,Jianjun Han
DOI: https://doi.org/10.1016/j.jnoncrysol.2022.122113
2022-12-30
Abstract:Transparent glass-ceramic in the SiO 2 -Li 2 O-Na 2 O-Al 2 O 3 -BaO-P 2 O 5 -ZrO 2 system were prepared by the three-stage heat treatment process. The effects of Al 2 O 3 content on the crystallization behavior, microstructure, and physical properties of the glass-ceramics were investigated by differential scanning calorimeter (DSC), X-Ray Diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and field emission scanning electron microscope (SEM). As the Al 2 O 3 increases from 4 to 7 mol%, all the Al 3+ ions are present in the [AlO 4 ] tetrahedra and participate in the glass network, resulting in the more compact structure of glass. The increasing in the glass network connectivity leads to the higher crystallization activation energy, hindering the formation of lithium disilicate and promoting the precipitation of Al-containing crystalline phases. The main crystalline phase of glass-ceramics transform from lithium disilicate and petalite to Li x Al x Si 1-x O 2 , and the transmittance of glass-ceramics decrease. Upon the three-steps heat treatments of 540°C/4h + 610°C/2h + 730°C/4h, the glass-ceramic with 4 mol% Al 2 O 3 containing petalite and lithium disilicate crystals shows high transparency of ∼85% in the visible light range, high hardness 8.07 GPa, and fracture toughness of 1.37 MPa·m 1/2 , which shows great potential in the applications of protective material for mobile devices.
materials science, multidisciplinary, ceramics