Abstract:A novel two‐step joining method was developed to join alumina ceramics for high‐temperature applications. Firstly, alumina ceramics were bonded using Al2O3 powder at 1550°C. Subsequently, the Dy2O3‐Al2O3‐SiO2 glass was infiltrated into the interlayer at 1450°C to obtain the alumina/alumina joints with dense composite interlayer composed by Al2O3, Dy2Si2O7, and few glass phase. The flexural strength of the joints at 1000°C reached about 90% of that of alumina ceramics under the same conditions. After the thermal cycles from room temperature to 1000°C for 50 times, there was no significant change in the flexural strength of the joints. In this work, a novel two‐step joining method was developed to join alumina ceramics for high‐temperature applications. First, alumina ceramics were bonded using Al2O3 powder at 1550°C. Subsequently, the Dy2O3–Al2O3–SiO2 glass was infiltrated into the interlayer at 1450°C to obtain the alumina/alumina joints with dense composite interlayer composed by Al2O3, Dy2Si2O7, and few glass phase. The content of Al2O3 in the composite interlayer reached 52.7%. As a result, the coefficient of thermal expansion mismatch between the interlayer and the alumina ceramic was reduced to only 2%. The flexural strength of the joints at room temperature was equivalent to that of the alumina ceramic. Furthermore, the flexural strength of the joints at 1000°C reached about 90% of that of alumina ceramics under the same conditions. After the thermal cycles from room temperature to 1000°C for 50 times, there was no significant change in the flexural strength of the joints.

Joining transparent spinel ceramics using refractive index–matched glass

Novel design of sapphire/spinel transparent ceramic joints with double glass interlayers by coating and bonding

Microstructure, mechanical and optical properties of MgAl2O4/MgAl2O4 joints bonded using CaO-Al2O3-SiO2 glass filler

Enhanced bonding strength of Al2O3/AlN ceramics joined via glass frit with gradient thermal expansion coefficient

Crystallization Behavior of Glass Ceramic Filler During Joining Process

High-performance flash joining of MgAl2O4 transparent ceramics

Joining Pre-Oxidized Dense Si3N4 to Porous Si3N4 with Β-Spodumene Based Glass-Ceramic Interlayer

Joining Dense Si3N4 to Porous Si3N4 Using a Novel Glass-Ceramic Interlayer with Precipitated Β-Lialsi2o6/mg2sio4

Joining of Porous Alumina with a CaO–Al2O3–SiO2 Glass‐Ceramic

Synthesis, Structure and Properties of MgO-Al2O3-SiO2-B2O3 Transparent Glass-Ceramics

Novel two‐step method for joining alumina ceramic by using Al2O3 powder followed by glass infiltration

Highly transparent MgAl0.5Ga1.5O4 ceramic for overcoming the trade-off between infrared transmittance and mechanical properties

Crystallization kinetics, structural and mechanical properties of transparent lithium aluminosilicate glass-ceramics

Crystallization and Wetting Behavior of Bismuth–borate–zinc Glass and Its Application in Low Temperature Joining Alumina Ceramics

Joining MgAl2O4 ceramics using ZnO–Al2O3–SiO2 glass ceramic with precipitated ZnAl2O4

Interfacial evolution mechanism of MgAl2O4/MgAl2O4 joints bonded with lanthanum glass

Joining of SiC ceramics using CaO-Al2O3-SiO2 (CAS) glass ceramics

Microstructure and crystallization behavior of Na2O-Al2O3-SiO2 glass-ceramics with MgO additions

Crystallization Behavior and Thermal Properties of B2O3–containing MgO-Al2O3-SiO2-Li2O Glass-Ceramic and Its Wettability on Si3N4 Ceramic

Joining of SiC ceramics using CaO-Al<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> (CAS) glass ceramics

Microstructure and ion‐exchange properties of transparent glass–ceramics containing Mg2SiO4 crystals