Peritectic Solidification Kinetics and Mechanical Property Enhancement in a Rapidly Solidified Ti–48 at% Al–8 at% Nb Alloy via Hierarchical Twin Microstructure

Chen Liang,HaiPeng Wang
DOI: https://doi.org/10.1002/adem.202100101
IF: 3.6
2021-05-18
Advanced Engineering Materials
Abstract:<p>The strength and ductility trade‐off dilemma has limited the wide application of TiAl‐based alloys. Here, a new insight into the potential for increasing the strength and ductility in a hypo‐peritectic Ti‐48 at.% Al‐8 at.% Nb alloy is accomplished by the electromagnetic levitation technique (EML). Moreover, a systematic analysis of the primary and subsequent peritectic solidification kinetics are conducted in the undercooling range of 308 K. Assisted with a high‐speed camera, an <i>in‐situ</i> observation for the liquid‐solid (primary β‐Ti phase and peritectic α‐Ti phase) interface migration is accomplished. When the alloy melt is undercooled to be 240 K, high‐ordered nanotwins were observed in Ti‐48 at.% Al‐8 at.% Nb alloy, which forms a unique hierarchical microstructure. Upon further increasing the undercooling, the density of these nanotwins is significantly enhanced. The room‐temperature compression results reveal that the strength and ductility increase up to 140% and 150%, respectively. This is mainly ascribed to the remarkable grain refinement, the formation of nanotwins with various orientation, the accumulation of dislocations and stacking faults, and the retention of metastable γ phase. The superior combination of strength and ductility indicates the possibility to fabricate high‐ordered nanotwins via rapid solidification, thus improving the performance of γ‐TiAl based alloys.</p><p>This article is protected by copyright. All rights reserved.</p>
materials science, multidisciplinary
What problem does this paper attempt to address?