Improving the ductility of high-strength multiphase NiAl alloys by introducing multiscale high-entropy phases and martensitic transformation

Yichao Zhu,Shangcheng Zhou,Liang Wang,Yao-Jian Liang,Yunfei Xue,Lu Wang

DOI: https://doi.org/10.1016/j.msea.2021.140949

2021-03-01

Abstract:<p>Including ductile solid-solution phases into NiAl intermetallic alloys can toughen these materials, but based on conventional alloying strategy, this approach either degenerates the strength or has no visible improvement in the room-temperature (RT) ductility. Here we show a feasible strategy to improve the RT ductility of NiAl alloys by replacing conventional dilute solid solutions with complex concentrated (<em>i.e.</em>, high-entropy) solid solutions as the ductilizing phases. The resulting alloy possesses a composite nanostructure, which combines B2-structured Ni(Al, Fe) phase with body-centered-cubic (BCC) and face-centered-cubic (FCC) structured high-entropy phases (HEPs) in different scales. We find that the applied stress is mainly partitioned to the B2 phase, contributing the alloy to high strength, while the ductile BCC and FCC HEPs, although bearing low loading, cooperate with the stress-induced martensitic transformation to accommodate the deformation, enhancing the sample ductility. Accordingly, our alloy presents superior tensile properties in a wide temperature range, including high strength (&gt;1500MPa at RT and &gt;360MPa at 700°C) and good ductility (&gt;9% at RT and ∼8% at −50°C), which achieves a simultaneous improvement in the ductility and strength compared with the conventional multiphase NiAl alloys.</p>

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering