Enhancing Strength-Ductility Synergy in Metastable Β-Ti Alloys Through Β-Subgrains-mediated Hierarchical Α-Precipitation
Yujie Xing,Dingxuan Zhao,Jinwen Lei,Youchuan Mao,Zehua Zheng,Wei Chen,Jinyu Zhang,Xianghong Liu,Jun Sun
DOI: https://doi.org/10.1016/j.jmst.2024.08.048
2025-01-01
Abstract:Titanium alloys can achieve ultrahigh strength through precipitation hardening of secondary alpha-phase (alpha s) from ,B-matrix but often compromise ductility due to the conventional strength-ductility trade-off. In this study, a new strategy based on ,B-subgrains-mediated hierarchical alpha-precipitation is devised to balance the conflict in Ti-6Al-2Mo-4Cr-2Fe (wt.%) alloy through a unique combination of hot rolling, short-term solid solution, and aging treatment, i.e., RSST + A. Tensile testing reveals that the RSST + A samples exhibit ultrahigh strength of similar to 1581 MPa and decent ductility of similar to 8.4 %, surpassing similar to 1060 MPa and similar to 2.7 % of the corresponding RSST counterparts without final aging treatment. This remarkable strengthening and counterintuitive ductilizing is attributed to the architecting of ,B-subgrains-mediated hierarchical alpha- precipitates as a result of our specific processing approach. The designed short-term solution introduces abundant ,B subgrains that are transformed from the retained intensive dislocations during hot rolling. The ,B subgrain boundaries subsequently promote a dramatic precipitation of alpha allotriomorphs (alpha GB) and Widmanst & auml;tten side-plates (alpha WGB), which effectively subdivides ,B grains into numerous tiny independent deformation units. Consequently, plastic strain is uniformly partitioned into a large number of small aged ,B subgrains during tension, which strongly impedes strain localization that would typically occur across multiple ,B subgrains in the fashion of long straight slip bands in the case of the RSST samples. Furthermore, the hierarchical alpha structure also postpones uncontrollable cracking even when structural damage occurs at the last stage of straining. These findings demonstrate that appropriately manipulating microstructure through elaborately designing processing routes enables unexpectedly ductilizing high- strength titanium alloys in the precipitation-hardening state. (c) 2024 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.