Enhanced strength of dual-phase Ti6242 alloy via a heterogeneous microstructure

Tingyi Lin,Lei Zhou,Pingwei Xu,Yingfei Guo,Hang Luo,Zhihai Cai,Haidou Wang,Jing Li,Yilong Liang,Yu Liang

DOI: https://doi.org/10.1016/j.matdes.2023.111972

2023-05-04

Abstract:In α+β titanium alloys, increasing the amount of α/β phase boundaries via conventional heat treatment usually improves the strength but significantly deteriorates the alloy's ductility. Instead of homogeneous β transformation microstructure (β t ) in conventional equiaxed microstructure (EM), two types of microstructures with heterogeneous β t are obtained via insufficient diffusion of alloying elements induced by rapid heat treatment (RHT), forming a unique semi-equiaxed structure (S-ES) in the Ti6242 alloy. Such microstructural characteristics, including the Type I microstructure characterized by a wavy interface between primary α phase (α p ) and heterogeneous β t , and the Type II microstructure, featuring heterogeneous β t embedded in the surrounding homogeneous β t structures, exhibit an enhanced strength with an insignificant loss of ductility. The enhanced strength is attributed to the increased fraction of α/β phase boundaries and precipitated residual β nanoparticles, whereas good ductility is obtained due to the soft α p , coherent β nanoparticles, and deformable β lamellae in the heterogeneous β t . However, the excessive presence of the Type II microstructure can deteriorate ductility to some extent. This work provides a novel approach to achieving high-performance dual-phase titanium alloys and being potentially applicable to other α+β titanium alloys.

materials science, multidisciplinary