Strengthening of a Near β-Ti Alloy through β Grain Refinement and Stress-Induced α Precipitation

Wei Chen,Chao Li,Kangtun Feng,Yongcheng Lin,Xiaoyong Zhang,Chao Chen,Kechao Zhou

DOI: https://doi.org/10.3390/ma13194255

IF: 3.4

2020-09-24

Materials

Abstract:Near β-Ti alloys with high strength and good ductility are desirable for application in aviation and aerospace industries. Nevertheless, strength and ductility are usually mutually exclusive in structural materials. Here we report a new thermo-mechanical process, that is, the alloy was cross-rolled in β field then aged at 600 °C for 1 h. By such a process, a high strength (ultimate tensile strength: 1480 MPa) and acceptable ductility (elongation: 10%) can be simultaneously achieved in the near β-Ti alloy, based on the microscale β matrix and nanoscale α phase. The microstructure evolution, mechanical properties and strengthening mechanisms have been clarified by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results showed that the grain size of the β phase progressively decreased with the increasing of rolling reduction. Moreover, dense dislocation structures and martensite phases distributed in the cross-rolled β matrix can effectively promote the precipitation of nanoscale α particles. TEM analyses confirmed that a heat-treatment twin was generated in the newly formed α lath during aging. These findings provide insights towards developing Ti alloys with optimized mechanical properties.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

This paper mainly discusses how to enhance the strength and ductility of near β-Ti alloy using specific thermomechanical processing methods. A new thermomechanical treatment process is proposed, which involves cross-rolling the alloy in the β phase and then aging at 600°C for 1 hour. This method successfully achieves a combination of high strength (1480 MPa tensile strength) and acceptable ductility (10% elongation) in near β-Ti alloy.

The study finds that with increasing cross-rolling deformation, the grain size of the β phase gradually decreases, and dense dislocation structures and martensitic phases are generated in the cross-rolling β matrix, which effectively promotes the precipitation of nano-sized α phase. During aging, heat-treated twins form within the newly formed α lamellae, which contribute to the strengthening effect on the mechanical properties of the material.

The paper also provides a detailed analysis of microstructural evolution, mechanical properties, and strengthening mechanisms, including phenomena such as dislocation slip, twin formation, and stress-induced martensitic transformation. Characterization using scanning electron microscopy (SEM) and transmission electron microscopy (TEM) reveals the crucial role of grain refinement and nano-sized α precipitates in improving the overall performance of the alloy.

In conclusion, this study proposes a new approach that provides a new perspective for optimizing the mechanical properties of titanium alloys, particularly in achieving a balance between high strength and good ductility.