A new microstructural refinement mechanism of ultra-large β grains in near-β titanium alloys during primary hot-working

Xianghong Liu,Tao Wang,Xiaolong Ren,Jie Fu,Liang Cheng,Kaixuan Wang

DOI: https://doi.org/10.1016/j.matlet.2023.134500

IF: 3

2023-05-11

Materials Letters

Abstract:In this work, the multi-step hot-working of a near-β titanium alloy, Ti-55511 alloy with centimeter-sized grains, was performed at 1170 °C. It was confirmed that the static/metadynamic recrystallization during interpass annealing was the primary mechanism responsible for the microstructural refinement. Meanwhile, a new breakdown mechanism of the ultra-large β grains with preferential orientation was observed during deformation, which was essentially different from the traditional discontinuous or continuous dynamic recrystallization. That is, new grain boundaries and even boundary networks were produced interconnecting the corners/protrusions of the -orientated grains through a low-angle grain boundary merging mechanism, which progressively severed the large β grains into smaller ones. Such a breakdown mechanism may be an important complement for microstructural refinement during primary hot-working, which allowed the breakdown of the ultra-large β grains under fairly low strain level.

materials science, multidisciplinary,physics, applied