Microstructure refinement of Ti-40Al-8Nb alloys via the decomposition of the metastable B2 phase at 1000 °C

Guang Yang,Xiaoxiao Yang,Hongchao Kou,Liang Cheng,Yuzhi Li,Yanhui Liu,Pujian Tian,Yanling Yang

DOI: https://doi.org/10.1016/j.jallcom.2020.155575

IF: 6.2

2020-10-01

Journal of Alloys and Compounds

Abstract:<p>In this study, a metastable microstructure composed of the single B2 phase was produced in Ti-40Al-8Nb (at. %) alloys by water quenching from 1400 °C. After annealing the fully-B2 microstructure at 1000 °C for 600 min, a refined microstructure composed of α₂, γ and B2 phases was obtained. Detailed analysis demonstrated that both the lath-liked coherent α₂ phase and equiaxed incoherent α₂ phase formed in the B2 matrix within a short time. During the subsequent tempering process, nanoscale γ lamellar precipitated from the coherent α₂ phase. Due to the large stored energy in the ultra-thin lamellar structures, the recrystallization of the γ phase happened, resulting in the globalization of the lamellar structures. Besides, γ twins also formed in the B2 matrix by following the Kurdjumov-Sachs (K-S) orientation relationships. With the increase of isothermal holding time, the coarsening of the α₂ and γ phases occurred, leading to a refined microstructure with the average grain size of 2 μm.</p>

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

This paper mainly discusses the problem of refining the microstructure of Ti-40Al-8Nb alloy by decomposing the unstable B2 phase at 1000°C. In the study, the authors first obtained a single B2 phase metastable structure by water quenching from 1400°C. Then, this fully B2 phase structure was annealed at 1000°C, and it was observed that a refined microstructure composed of a2, g, and B2 phases was formed after 600 minutes of annealing, with an average grain size of about 2 microns. During this process, lath-like homogeneous a2 phase and equiaxed heterogeneous a2 phase rapidly formed in the B2 matrix, and nanoscale g-layer precipitates were precipitated from the homogeneous a2 phase. Due to the large amount of stored energy in the ultra-thin layered structure, recrystallization of the g phase occurred, forming a globular layered structure. In addition, g twinning conforming to the Kurdjumov-Sachs orientation relationship was observed to form in the B2 matrix. With the increase of isothermal holding time, the a2 and g phases coarsened, further refining the microstructure.

The study found that the unstable B2 phase decomposes and produces a refined structure without the u0 phase at 1000°C, which is caused by a large degree of supercooling (244°C). In the subsequent annealing process, the a2 phase transformed into a nanoscale lamellar structure due to a high density of stacking faults, promoting the precipitation and refinement of the g phase. Meanwhile, the g phase not only precipitated directly from the B2 matrix, but also formed from the interfaces of the heterogeneous a2 phase and the homogeneous a2 phase, ultimately forming a refined microstructure without the u0 phase. By analyzing samples annealed for different times, the detailed evolution process of the microstructure over time was revealed.