Nucleation And Growth Of Alpha Phase In A Metastable Beta-Titanium Ti-5al-5mo-5v-3cr Alloy: Influence From The Nano-Scale, Ordered-Orthorhombic O '' Phase And Alpha Compositional Evolution

Baptiste Gault
DOI: https://doi.org/10.1016/j.scriptamat.2020.113672
IF: 6.302
2021-01-01
Scripta Materialia
Abstract:We investigated the nucleation and growth of alpha precipitates in the presence of nano-scale, titanium-rich, ordered-orthorhombic O '' precipitates formed during heating at 5 degrees C/min to 400 degrees C in a metastable beta-Ti alloy, Ti-5Al-5Mo-5V-3Cr. The O '' precipitates are found to assist alpha nucleation by serving as preferential nucleation sites. In the very initial stages of its precipitation, the alpha phase is found to have formed via a coupled diffusional-displacive mode as titanium-rich plates. At this stage, aluminum partitions equally between the beta matrix and the growing alpha precipitates, but slowly diffuses up-hill into the alpha phase during isothermal aging at 400 degrees C for 15 h. The interplay between such pre-formed metastable phases and alpha can be exploited to tailor the microstructure, by refining the alpha distribution, and consequently improve the mechanical properties of beta-Ti alloys. Our work paves the way for exploiting this cascade of metastable phases for further microstructural engineering of beta-Ti alloys. (C) 2020 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
What problem does this paper attempt to address?