Fabrication of Highly Heterogeneous Precipitate Microstructure in an Α/β Titanium Alloy
Yandi Jia,Huhu Su,Shuo Cao,Rongpei Shi,Yingjie Ma,Qian Wang,Sensen Huang,Ruixue Zhang,Qingmiao Hu,Yufeng Zheng,Shijian Zheng,Jiafeng Lei,Rui Yang
DOI: https://doi.org/10.1016/j.actamat.2024.120302
IF: 9.4
2024-01-01
Acta Materialia
Abstract:To obtain a synergistic combination of high strength and high ductility in titanium alloys, design and creation of heterogenous precipitate microstructure have attracted increasing attention. Herein, using Ti-3Al-5Mo-4.5V (wt. %, an alpha/(1 titanium alloy) as a model alloy, we demonstrated that a highly heterogenous alpha-phase precipitate microstructures with well-controlled length scale of spatial heterogeneity (i.e., micron-sized primary alpha and nanoscale secondary alpha precipitates), can be synthesized through activating the omega-assisted alpha nucleation transformation pathway that operates in metastable (1 titanium alloy alone. A detailed analysis of transformation pathway for omega phase and the underlying omega-assisted alpha nucleation mechanisms is carried out using the integrated advanced characterizations, theoretical calculations and simulations based on DFT, and phase-field modeling. Experimental results show unambiguously that the embryonic omega particles (also known as athermal omega) with partially collapsed structure are incapable of refining secondary alpha (alpha s). In contrast, the isothermal omega particles with a complete structural collapse play an important role in assisting alpha s nucleation, resulting in the formation of the ultrafine alpha s lamellae at nanoscales after two-step aging heat treatments. The contributions from the isothermal omega particles are then quantified using first-principles calculations and phase-field simulations. It is found that, even though the solute partitioning between a growing isothermal omega particle reduces the alpha s nucleation driving force in the surrounding beta matrix, the elastic interaction between the omega particles and the alpha s nucleus provides more driving force for alpha s nucleation at specific locations of the omega/beta interface. Our work extends the microstructure design strategy based on omega-assisted alpha nucleation mechanism from metastable (1 to alpha/(1 Ti-alloys, thereby significantly widening the application space of the strategy.