Abstract:The paper comprehensively describes the evolution of metastable microstructures in a cast low-Ta-containing γ-TiAl alloy during cooling-tempering-lamellarization heat treatments. The behavior and mechanism of microstructure refinement are discussed. The rapid cooling generates metastable microstructures, including Widmanstätten, feathery, and massive structures, with many γ variants in small sizes and different orientations. It significantly refines the coarsened colonies and randomizes the texture. The tempering can effectively stabilize the metastable microstructures. During tempering, the γ→α phase transformation is more active at higher temperatures while coarsening and recrystallization dominate at lower temperatures. After tempering, a refined microstructure with spherical grains and convoluted structures forms. Subsequent lamellarization treatment optimizes the microstructure and obtains a fine-grained nearly-lamellar microstructure with small colonies (∼70 μm) and dispersed fine γ grains (∼10 vol%), which yielded a 1.0 % elongation with a 487 MPa yield strength (0.2%) and a 589 MPa ultimate tensile strength at room temperature. Finally, the unique promotion effects and mechanism of a small amount of Ta addition on the nucleation, growth, evolution, and stabilization of metastable microstructures are concluded and discussed, which is crucial for the refinement of cast γ-TiAl alloy by heat treatment alone.

Grain refinement of 1 at.% Ta-containing cast TiAl-based alloy by cyclic air-cooling heat treatment

Metastable microstructure evolution and grain refinement in a Low-Ta containing γ-TiAl alloy through heat treatment

On the grain size refinement of TiAl alloys by cyclic heat treatment

Grain refinement of a Ti–47Al–8Nb–2Cr alloy through heat treatments

Grain refinement of a TiAl alloy by heat treatment through near gamma transformation

Control of the homogeneity of the lamellar structure of a TiAl alloy refined by heat treatment

Refining grain size of a TiAl alloy by cyclic heat treatment through discontinuous coarsening

Effect of cooling rate on the grain refinement of TiAl-based alloys by rapid heat treatment

Cycling Heat Treatment Refinement the Grain Size of a TiAl - Base Alloy

Control of a fine-grained microstructure for cast high-Cr TiAl alloys

Microstructure refinement of a TiAl alloy by beat treatment

Refining grain of as-cast Ti46A18Nb alloy by heat treatment

Metastable transformation behavior in a Ta-containing TiAl-Nb alloy during continuous cooling

Grain Refinement Mechanism at High Undercooling of Ni80Cu20 Alloy

Adjusting the /<sub>2</sub> and Ti<sub>2</sub>AlC phase on microstructure evolution and improving mechanical properties at room and elevated temperatures with the addition of Ta

Grain Refinement by Trace Tib2 Addition in Conventional Cast Tial-Based Alloy

Microstructure refinement of Ti-40Al-8Nb alloys via the decomposition of the metastable B2 phase at 1000 °C

Effect of heating rate on the grain refinement of a TiAl alloy by cyclic heat treatment

Refinement mechanism of centimeter-grade coarse grains in as-cast Ti 2 AlNb-based alloy during multi-directional forging

The Effect of Refined Coherent Grain Boundaries on High-Temperature Oxidation Behavior of TiAl-Based Alloys through Cyclic Heat Treatment

Achieving fine fully lamellar microstructure of casting TiAl alloy by simple heat treatment