Multistep evolution of βo phase during isothermal annealing of Ti-42Al-5Mn alloy: Formation of Laves phase

Hongjian Tang,Xiaobing Li,Yingche Ma,Bo Chen,Weiwei Xing,Pengxiang Zhao,Lei Shu,Mengshu Zhang,Kui Liu
DOI: https://doi.org/10.1016/j.intermet.2020.106932
IF: 4.075
2020-11-01
Intermetallics
Abstract:<p>Intermetallic β-solidifying γ-TiAl alloys exhibit improved hot workability owing to the presence of soft β phase at elevated temperature. However, through the incorporation of essential β-stabilizers the metastable ordered β phase (β<sub>o</sub>) is retained and hence an understanding of its phase transformation behavior at target temperature is indispensable. Here we report new insights into the multistep evolution of the β<sub>o</sub> phase during isothermal annealing of Ti-42Al-5Mn (at.%) alloy at 800 °C. Our observations reveal that both irregularly shaped α<sub>2</sub> and γ platelets are firstly precipitated from the interior of β<sub>o</sub> phase, accompanied with Mn rejection to the surrounding. And this contributes to the local enrichment of Mn, which thereupon leads to intragranular precipitation of secondary phase particles (SPPs). More specifically, an ellipsoidal submicrometre-scale Mn-rich Laves phase with a C14 hexagonal structure formed at the expense of α<sub>2</sub> precipitates via a shuffle of atoms is detected. The Laves phase has an orientation relationship (OR) with the parent α<sub>2</sub> phase described as [10<span class="math"><math>1¯</math></span>0]<sub>α2</sub>//[11<span class="math"><math>2¯</math></span>0]<sub>Laves</sub>, (0001)<sub>α2</sub>//(1<span class="math"><math>1¯</math></span>00)<sub>Laves</sub>. It is due to the instability of partial pre-formed γ precipitates that assists the solution of Al in Laves phase forming the formula Ti(Al,Mn)<sub>2</sub>, thereby facilitating the growth of Laves phase.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
What problem does this paper attempt to address?