Hierarchical microstructure and strain partition of a PM α + β titanium alloy with an ultrahigh strength-ductility synergy

Bowen Zhang,Xiaogang Wu,Deliang Zhang

DOI: https://doi.org/10.1016/j.matchar.2023.112835

IF: 4.537

2023-03-24

Materials Characterization

Abstract:Powder metallurgy (PM) α + β Ti-4Al-4Mo-4Sn-0.5Si alloys were fabricated through thermomechanical powder consolidation of TiH 2 -based powder compacts with two different processing routes: one involving blending the elemental powders (BE route) and the other involving mechanical milling a blend of elemental powders (MM route). With the MM + annealing + solution and aging (STA) route, a hierarchical microstructure consisting of necklace-like micron-scaled grain boundary α (α GB ) segments and isolated submicron-scaled primary α (α p ) rods dispersed in a β transformed structure (β t ) matrix containing a high number density of nano-scaled secondary α (α s ) laths was produced in the alloy. The alloy with the hierarchical microstructure achieved an excellent combination of a very high yield strength of 1339 MPa,an ultimate tensile strength of 1467 MPa and an excellent ductility of 10.4%. The increased strength was mainly due to the high fraction of β t matrix in which the fine-dispersed α s precipitates with different orientations efficiently blocked the dislocation motion during deformation. The excellent ductility achieved despite of the high flow stress can be attributed to the elimination of strain concentration in the α GB segments which prevented their cracking prior to the material reaching the necking point during plastic deformation. This was in contrast with the typical α/β t lamellar microstructure of the same alloy composition obtained with the BE + same heat treatment route where strain concentration in the α GB plates occurred due to the direct slip transmission from α colonies to adjacent parent α GB grains during plastic deformation, thus resulting in intergranular premature cracking. TEM observation demonstrated that the strain gradient from the α/β t interfaces to the domain interiors of both α GB segments and α p rods activated a high density of geometrically necessary dislocations near the interfaces, and caused an obvious synergistic strengthening effect which also contributed to the slow drop of strain hardening rate and thus was beneficial to improving the ductility.

materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing