Abstract:Powder metallurgy (PM) α + β Ti-4Al-4Mo-4Sn-0.5Si alloys were fabricated through thermomechanical powder consolidation of TiH 2 -based powder compacts with two different processing routes: one involving blending the elemental powders (BE route) and the other involving mechanical milling a blend of elemental powders (MM route). With the MM + annealing + solution and aging (STA) route, a hierarchical microstructure consisting of necklace-like micron-scaled grain boundary α (α GB ) segments and isolated submicron-scaled primary α (α p ) rods dispersed in a β transformed structure (β t ) matrix containing a high number density of nano-scaled secondary α (α s ) laths was produced in the alloy. The alloy with the hierarchical microstructure achieved an excellent combination of a very high yield strength of 1339 MPa,an ultimate tensile strength of 1467 MPa and an excellent ductility of 10.4%. The increased strength was mainly due to the high fraction of β t matrix in which the fine-dispersed α s precipitates with different orientations efficiently blocked the dislocation motion during deformation. The excellent ductility achieved despite of the high flow stress can be attributed to the elimination of strain concentration in the α GB segments which prevented their cracking prior to the material reaching the necking point during plastic deformation. This was in contrast with the typical α/β t lamellar microstructure of the same alloy composition obtained with the BE + same heat treatment route where strain concentration in the α GB plates occurred due to the direct slip transmission from α colonies to adjacent parent α GB grains during plastic deformation, thus resulting in intergranular premature cracking. TEM observation demonstrated that the strain gradient from the α/β t interfaces to the domain interiors of both α GB segments and α p rods activated a high density of geometrically necessary dislocations near the interfaces, and caused an obvious synergistic strengthening effect which also contributed to the slow drop of strain hardening rate and thus was beneficial to improving the ductility.

Extraordinary tensile properties of titanium alloy with heterogeneous phase-distribution based on hetero-deformation induced hardening

Achieving Enhanced Tensile Strength-Ductility Synergy Through Phase Modulation in Additively Manufactured Titanium Alloys

Enhanced strength of dual-phase Ti6242 alloy via a heterogeneous microstructure

Heterostructures Enhance Simultaneously Strength and Ductility of a Commercial Titanium Alloy

Simultaneously enhancing strength and ductility of HCP titanium via multi-modal grain induced extra dislocation hardening

Making high primary α phase content titanium alloy exceptional strength and ductility by designing the heterogeneous structure

Homogeneous α-precipitation and enhanced plasticity in Ti–6Cr–5Mo–5V–4Al high-strength metastable titanium alloy with heterogenous β-structure

Designing ultra-strong and ductile hierarchical titanium alloys via interstitial solute-mediated multi-morphologic α-nanoprecipitates

Hierarchical microstructure and strain partition of a PM α + β titanium alloy with an ultrahigh strength-ductility synergy

Additive manufacturing of titanium alloys with enhanced strength and uniform ductility via multi-element alloying

Improving strain hardening capacity of high-strength Ti–6Al–4V alloy by a dual harmonic structure

Superior strength-ductility synergy by microstructural heterogeneities in pure titanium

Towards strength-ductility enhancement of titanium matrix composites through heterogeneous grain structured Ti matrix design

Introducing β-Ti ductile-zones for enhancing both strength and ductility in heterostructured titanium alloy composites

Microstructure evolution and mechanical property of a new multi-component β titanium alloy with ultrahigh strength above 1350 MPa

Achieving high strength-ductility synergy in a hierarchical structured metastable β-titanium alloy using through-transus forging

Fabrication of Highly Heterogeneous Precipitate Microstructure in an Α/β Titanium Alloy

Mechanical properties and microstructure of heterogeneous commercial pure titanium prepared by rotary swaging and annealing

Enhanced strength-ductility synergy and mechanisms of heterostructured Ti6Al4V-Cu alloys produced by laser powder bed fusion

Sustaining an excellent strength-ductility combination of a PM α + β titanium alloy with fine prior β grains and heterogeneous microstructure

Multiple deformation mechanisms induce high work hardening in Ti–5Al–7.5 V alloy via transformed β matrix