Multiple deformation mechanisms induce high work hardening in Ti–5Al–7.5 V alloy via transformed β matrix

Sisi Xie,Zhihong Wu,Nana Chen,Mingxiang Zhu,Hao Yang,Zilong Zhang,Chuanyun Wang,Jinshan Li,Hongchao Kou

DOI: https://doi.org/10.1080/21663831.2024.2320767

2024-02-27

Materials Research Letters

Abstract:In this work, different transformed β matrix was obtained in Ti–5Al–7.5 V alloy. The alloy with equiaxed α p phase and transformed β matrix containing α′ martensite and β phase exhibits good combination of strength and plasticity, as well as a high work hardening rate. A concurrent operation of stress-induced α′′ martensitic transformation, deformation twinning and dislocation slips was observed governing the deformation process of this alloy. The alloy with equiaxed α p phase and transformed β matrix containing secondary α s plates and retained β phase shows a high strength and plasticity but low work hardening rate, which is caused by dislocation slips. Highlights The quenched Ti–5Al–7.5 V alloy exhibits a high work hardening rate, approximately 5500 MPa. The dependence of work hardening rate of Ti–5Al–7.5 V alloy on transformed β matrix is revealed. Concurrent operations of stress-induced α′′ martensitic transformation, deformation twinning and dislocation slips govern deformation of the studied alloy.

materials science, multidisciplinary