Abstract:Ti44Al6Nb1.0Cr2.0V alloy was directionally solidified (DS) with cold crucible under different input powers (40 kW, 45 kW, 48 kW and 50 kW; corresponding to temperature gradient of 15.2 K/mm, 21.0 K/mm, 22.9 K/mm, 25.5 K/mm) and the same pulling velocity (8.33 mu m/s). The results show that all the DS samples have the beta-solidification characteristics and when the power is 45 kW or 48 kW, they have the well-DS macrostructure. After DS, the lamellar width becomes smaller and more homogeneous from the as-cast 1650 +/- 1200 nm to less than 710 +/- 376 nm. The higher the power is, the smaller the lamellar width it has. The original casting microcracks can be eliminated after DS and the percentage of small angle lamellas is higher for the well-DS samples. For the DS samples, the nanoindentation hardness in lamella region and the lamellar width yield the relationships of H-N = 16.12d(-0.127) and r(2) = 0.992. When the as-cast and heat treatment (HT) conditions are considered, the relationships are changed as H'(N) = 16.09d'(-0.127) and r'(2) = 0.971. The nanoindentation hardness of B-2 phase and block gamma phase keep almost the same respectively under the different conditions. RT tensile property is improved to average UTS 589.4 MPa and average elongation 1.16% after DS (P = 45 kW) comparing with the original as-cast 498.8 MPa and 0.53%. Trans-granular and trans-lamella fracture is the main fracture mode for the DS samples. After annealing (at 1250 degrees C, 1300 degrees C, 1350 degrees C), lamellar width is coarsen to more than 2002 +/- 1286 nm; B-2 phase segregation is reduced obviously, but some new microcracks form; HT samples exhibits a poor RT tensile property, in which the HT2 sample has a relatively higher property and it yields the average UTS 440.6 MPa and average elongation 0.45%. (C) 2015 Elsevier B.V. All rights reserved.

A Newly Generated Nearly Lamellar Microstructure in Cast Ti-48Al-2Nb-2Cr Alloy for High-Temperature Strengthening

Microstructure Evolution and Nano-Precipitate of Multi-Stage Heat-Treated Ti–45Al–2Nb–2Cr-0.3C Alloy

Solidification Microstructure Evolution and Mechanical Properties of Casting Ti-48Al-2Cr-2Nb-(Ni,TiB2)Alloy

Microstructure evolution, hot deformation behavior and mechanical properties of Ti-43Al-6Nb-1B alloy

Microstructure Evolution and Tensile Properties of Conventional Cast TiAl-based Alloy with Trace Ni Addition

Microstructure Evolution of the Ti-46Al-8Nb-2.5V Alloy during Hot Compression and Subsequent Annealing at 900 °C

Breaking the high-temperature strength-ductility trade-off in TiAl alloys through microstructural optimization

Effects of cycle heat treatment on the microstructure and mechanical property of as-cast ?-TiAl alloy

Microstructure and room temperature tensile property of as-cast Ti44Al6Nb1.0Cr2.0V alloy

Effect of annealing treatment on microstructure and tensile properties of Ti-48Al-2Cr-5Nb alloy fabricated by laser additive manufacturing

Microstructural Control and Mechanical Properties of Ti–47Al–2Cr–2Nb Alloy by Directional Solidification Electromagnetic Cold Crucible Technique

Effect of Post-Heat Treatment on Ti2AlNb-based Alloy Fabricated by Twin-Wire Alternating Dual-Electron Beam Additive Manufacturing Technology

Tensile properties and fracture toughness of TiAl alloys with controlled microstructures

Compositional and Microstructural Optimization and Mechanical-Property Enhancement of Cast Ti Alloys Based on Ti-6Al-4V Alloy

Microstructure Evolution and Mechanical Properties of High Nb-TiAl Intermetallic Compounds during Heat Treatment

Microstructure and Mechanical Properties of Novel Ti-Al- Mn- W Alloy

Microstructure, Tensile Properties and Creep Behavior of High-Al TiAlNb Alloy Using Electromagnetic Cold Crucible Continuous Casting

Achieving super-high strength and acceptable plasticity for a near β-type Ti-4.5Mo-5.1Al-1.8Zr-1.1Sn-2.5Cr-2.9Zn alloy through manipulating hierarchical microstructure

Microstructure Evolution and Mechanical Properties of Directionally-Solidified TiAlNb Alloy in Different Temperature Gradients

Simultaneously Enhancing the Strength and Ductility of Lamellar Ti–6Al–4V Alloy Via Designing Hierarchical 3D Nanolayered Structure

Thermal stability and mechanical properties of Ti–22Al–25Nb alloy with different initial microstructures