Thermomechanical characterization and conventional rolling of a novel β-solidifying γ-TiAl alloy with excellent comprehensive properties

Junjie Hao,Kun Qian,Xiaobing Li,Peng Xue,Lei Shu,Bo Chen,Kui Liu

DOI: https://doi.org/10.1016/j.jmrt.2023.09.076

IF: 6.267

2023-09-01

Journal of Materials Research and Technology

Abstract:The development of the β-solidifying γ-TiAl alloys with good oxidation resistance and thermal deformation ability has always been crucial for the practical application. However, increasing the content of the antioxidant elements, such as Nb, Al, etc., tends to be detrimental to the deformability of the alloys. In this work, a novel Nb, Mn containing β-solidifying TiAl alloy with the nominal composition of Ti-43Al-1.5Mn-3Nb-0.2C-0.2Si-0.1B (at. %) (named as NbMn-TiAl) is invented, which goes through the single β phase as well as the α phase during solidification, resulting in the final as-cast microstructure of nearly full lamellar structure (NFL). Subsequently, the isothermal compression tests were performed within a temperature range of 1100 °C–1300 °C and a strain rate range of 0.001 s−1-10 s−1, the hot processing maps and constitutive equation were established. Moreover, the deformation mechanisms were clarified, including the bending/kinking of the α2/γ lamellar colonies, the dynamic recrystallization (DRX) of γ phase and α phase at different temperatures. Rolled bars with a diameter of 12 mm were then directly fabricated from the ingot by conventional hot rolling process. The as-rolled bars exhibited excellent oxidation resistance and mechanical properties that outperform many available TiAl alloys manufactured using various methods.

materials science, multidisciplinary,metallurgy & metallurgical engineering