Influence of Laser Energy Density on Tribological Properties of AlSi10Mg Manufactured by Selective Laser Melting

Keqing Wang
DOI: https://doi.org/10.3390/ma17020323
IF: 3.4
2024-01-10
Materials
Abstract:In recent years, much work related to the performance of AlSi10Mg manufactured by selective laser melting (SLM) has been extensively researched. However, the study of tribological performance caused by different laser energy densities is still insufficient. This work concentrates on the relationship between the wear resistance and laser energy density of AlSi10Mg processed using SLM. Moreover, XRD characterization, density, surface roughness and microhardness were also examined since they are closely related to wear resistance. The results revealed that the XRD pattern of AlSi10Mg was mainly composed of the α-Al and Si phases under the conditions of different laser energy densities. In addition, the peak of Mg2Si was also detected. Also, the grain size increased with the increasing of laser energy density. The increase in laser energy density led to an increase in the convection and porous phenomenon in the molten pool. However, when the value was lower, the overlapping area reduced, and the strength between adjacent melting paths was insufficient, resulting in the declination of the sample property. According to the experimental results, a laser energy density of 63.33 J/mm3 was considered to be a relative optimal condition. The relative density, Ra, microhardness and wear volume were 99.2%, 8.86 μm, 128.3 HV0.2 and 2.96 × 10−2 mm3, respectively. The worn surface morphology also confirmed the influence of laser energy density on wear resistance. A regression model was established and analyzed, which showed the reliability of the results. Furthermore, the tribological mechanism was also revealed.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
### Problems Addressed by the Paper This paper primarily explores the impact of different laser energy densities on the friction and wear performance of AlSi10Mg alloy manufactured through Selective Laser Melting (SLM). #### Specific Objectives: 1. **Relationship between laser energy density and wear resistance**: Investigate the changes in wear resistance of AlSi10Mg alloy under different laser energy densities. 2. **Microstructure analysis**: Analyze the microstructure under different laser energy densities using characterization methods such as X-ray diffraction (XRD). 3. **Density, surface roughness, and microhardness**: Examine the relationship between these parameters and wear resistance. 4. **Establish a regression model**: Validate the reliability of the experimental results and reveal the friction and wear mechanisms. #### Research Background: - AlSi10Mg alloy is widely used in aerospace, automotive, and marine industries due to its high thermal conductivity, low weight, and excellent mechanical properties. - Traditional forging or casting processes are time-consuming and cost-inefficient. - SLM technology is gaining attention due to its high degree of freedom and rapid prototyping capabilities. - Laser energy density, as a key parameter in the SLM process, significantly affects the microstructure and mechanical properties of the material. #### Main Findings: - Under different laser energy density conditions, the XRD patterns of AlSi10Mg alloy are mainly composed of α-Al and Si phases. - Increasing laser energy density leads to an increase in grain size. - When the laser energy density is 63.33 J/mm³, the sample's relative density, surface roughness (Ra), microhardness, and wear volume are 99.2%, 8.86 μm, 128.3 HV 0.2, and 2.96 × 10⁻² mm³, respectively. - The established regression model demonstrates the reliability of the results and reveals the friction and wear mechanisms. In summary, this paper aims to systematically study the impact of different laser energy densities on the friction and wear performance of AlSi10Mg alloy and establishes a reliable regression model based on experimental data.