Abstract:AlSi10Mg alloy was prepared by selective laser melting (SLM) using self-made AlSi10Mg powder as raw material. Optical microscope, scanning electron microscope, electron backscattering instrument, and x-ray diffractometer were used to compare and study the differences of microstructure and properties of AlSi10Mg alloy before and after heat treatment. The results show that the AlSi10Mg alloy formed by SLM is mainly composed of α-Al solid solution and network eutectic Si, and with a small amount of Mg 2 Si precipitates, the mechanical properties are better than those of traditional casting alloys. The molten pool is composed of fine grain zone, coarse grain zone and heat affected zone. The grain size of each zone is different. The center of the molten pool is mainly equiaxed grains randomly distributed, and the boundary of the molten pool is mainly columnar grains preferentially growing along , forming weak brass texture. With the increase of heat treatment temperature, the reticulate eutectic Si gradually dissolves and breaks into particles, and is further coarsened and spheroidized. The strength and hardness of the alloy decrease and the elongation increases. Columnar grains gradually transform into equiaxed grains, the preferred orientation of grains weakens and the texture gradually disappears. Due to the continuous slip and climbing of dislocations, the small-angle grain boundaries gradually change to large-angle grain boundaries, the average grain orientation difference increases, the proportion of low coincidence site lattice grain boundaries increases, and the intergranular corrosion resistance of the alloy is enhanced.

Research on the limitations of laser energy density and microstructure characteristics of selective laser melted AlSi10Mg alloy

Microstructure and Mechanical Properties of Selective Laser Melted Mg-9 Wt%al Powder Mixture

Parameter optimization and microhardness experiment of AlSi10Mg alloy prepared by selective laser melting

Effect of Processing Parameters on Tensile Properties and Microstructure of Selective Laser Melted AlSi10Mg Alloy

Influence of Laser Process on the Porosity-Related Defects, Microstructure and Mechanical Properties for Selective Laser Melted AlSi10Mg Alloy

The AlSi10Mg Samples Produced by Selective Laser Melting: Single Track, Densification, Microstructure and Mechanical Behavior

Experimental Research on Selective Laser Melting AlSi10Mg Alloys: Process, Densification and Performance

Achieving Superior Strength and Ductility of AlSi10Mg Alloy Fabricated by Selective Laser Melting with Large Laser Power and High Scanning Speed

Study on microstructure and properties of selective laser melting formed AlSi10Mg alloy

Process parameter optimization and mechanical properties for selective laser melting of AlSi10Mg alloy

Effect of process parameters on microstructures and properties of Al-42Si alloy fabricated by selective laser melting

Effect of Laser Energy Density on Surface Morphology, Microstructure, and Magnetic Properties of Selective Laser Melted Fe-3wt.% Si Alloys

Microstructure, metallurgical defects and hardness of Al–Cu–Mg–Li–Zr alloy additively manufactured by selective laser melting

Selective laser melting of Al-3.48Cu-2.03Si-0.48Sc-0.28Zr alloy: Microstructure evolution, properties and metallurgical defects

Influence of Laser Energy Density on Tribological Properties of AlSi10Mg Manufactured by Selective Laser Melting

Selective Laser Melting of Al-Cu-Mn-Mg Alloys: Processing and Mechanical Properties

Microstructure of Laser Surface Melting (LSM) Layers on Cast Al-Si Alloy

Effect of Heat Treatment on Microstructure and Properties of Selective Laser Melting AlSi10Mg Alloy

Microstructure, wear and residual stresses of selective laser melting AlSi10Mg solid cylinder

Impacts of Defocusing Amount and Molten Pool Boundaries on Mechanical Properties and Microstructure of Selective Laser Melted AlSi10Mg

Influence of Mg Content on Microstructure Coarsening, Molten Pool Size, and Hardness of Laser Remelted Al(- x)-Mg-Sc Alloys